In this work, three kinds of ultrathin tremella-like MnO2 have been simply synthesized by decomposing KMnO4 under mild hydrothermal conditions. When applied as electrode materials, they all exhibited excellent electro...In this work, three kinds of ultrathin tremella-like MnO2 have been simply synthesized by decomposing KMnO4 under mild hydrothermal conditions. When applied as electrode materials, they all exhibited excellent electrochemical performance. The as- prepared MnO2 samples were characterized by means of XRD, SEM, TEM and XPS. Additionally, the relationship of the crystalline nature with the electrochemical performance was investigated. Among the three samples, the product with the poorest crystallinity had the highest capacitance of 220 Fig at a current density of 0.1 A/g. It is thought that the ultrathin MnO2 nanostructures can serve as promising electrode materials for supercapacitors.展开更多
基金Acknowledgements This work was financially supported by the National Natural Science Foundation of China （Grant Nos. 51172119 and 51221291）, the graduate student innovation fund project in Jiangxi Province （No. YC2014-S301）, and the Jingdezhen Ceramic Institute graduate student innovation fund project.
文摘In this work, three kinds of ultrathin tremella-like MnO2 have been simply synthesized by decomposing KMnO4 under mild hydrothermal conditions. When applied as electrode materials, they all exhibited excellent electrochemical performance. The as- prepared MnO2 samples were characterized by means of XRD, SEM, TEM and XPS. Additionally, the relationship of the crystalline nature with the electrochemical performance was investigated. Among the three samples, the product with the poorest crystallinity had the highest capacitance of 220 Fig at a current density of 0.1 A/g. It is thought that the ultrathin MnO2 nanostructures can serve as promising electrode materials for supercapacitors.