An ultra-high ion-selective Nafion composite membrane modified by phosphotungstic acid(PWA)coupled silica for vanadium redox flow battery(VRB)was constructed and prepared through solution casting.The composite membran...An ultra-high ion-selective Nafion composite membrane modified by phosphotungstic acid(PWA)coupled silica for vanadium redox flow battery(VRB)was constructed and prepared through solution casting.The composite membrane exhibits excellent proton conductivity and vanadium ions blocking property by incorporating the nanohybrid composed of silica and PWA into the Nafion ionomer.Simple tuning for the filling amount of the nanohybrid endows the obtained membranes preeminent vanadium barrier property including a minimum vanadium permeability of 3.13×10-7cm2min-1and a maximum proton conductivity of 0.081 S cm-1at 25°C.These indicate an ion selectivity of 2.59×105S min cm-3,which is 6.8times higher than that of recast Nafion(0.33×105S min cm-3).As a result,the VRB with the composite membrane shows superior battery performance containing a lower self-discharge rate,higher capacity retention and more robust cyclic stability compared with recast Nafion over a range of current densities from 40 to 100 m A cm-2.展开更多
基金financially supported by the National Natural Science Foundation of China(Grant no.21273058,21673064,51802059 and 21503059)China postdoctoral science foundation(Grant no.2018M631938,2018T110307 and 2017M621284)+1 种基金Heilongjiang Postdoctoral Fund(Grant no.LBH-Z17074 and LBH-Z18066)Fundamental Research Funds for the Central Universities(Grant no.HIT.NSRIF.2019040 and 2019041)。
文摘An ultra-high ion-selective Nafion composite membrane modified by phosphotungstic acid(PWA)coupled silica for vanadium redox flow battery(VRB)was constructed and prepared through solution casting.The composite membrane exhibits excellent proton conductivity and vanadium ions blocking property by incorporating the nanohybrid composed of silica and PWA into the Nafion ionomer.Simple tuning for the filling amount of the nanohybrid endows the obtained membranes preeminent vanadium barrier property including a minimum vanadium permeability of 3.13×10-7cm2min-1and a maximum proton conductivity of 0.081 S cm-1at 25°C.These indicate an ion selectivity of 2.59×105S min cm-3,which is 6.8times higher than that of recast Nafion(0.33×105S min cm-3).As a result,the VRB with the composite membrane shows superior battery performance containing a lower self-discharge rate,higher capacity retention and more robust cyclic stability compared with recast Nafion over a range of current densities from 40 to 100 m A cm-2.