The alloying behavior and microstructures of the(CoCrFeNiMn)_(90)M_(10)(M=Al,Hf)high-entropy alloy(HEA)powders fabricated by mechanical alloying were studied.The CoCrFeNiMn)_(90)Al_(10) powders have duplex solid-solut...The alloying behavior and microstructures of the(CoCrFeNiMn)_(90)M_(10)(M=Al,Hf)high-entropy alloy(HEA)powders fabricated by mechanical alloying were studied.The CoCrFeNiMn)_(90)Al_(10) powders have duplex solid-solution structures.In contrast,nanocrystalline HfNi_(3) anchoring in amorphous structures is found in the(CoCrFeNiMn)_(90)Hf_(10) powders.The(CoCrFeNiMn)_(90)Al_(10) powders show better ferromagnetic behaviors,mainly explained by the facilitated motion of the magnetic domain induced by the coherent interface between duplex phases.Combined with our previous work,the rules of forming solid-solution and amorphous phase in as-milled HEA powders are preliminarily proposed.It is found that,compared with the as-cast HEA reported previously,the variation range of mixing enthalpy with atomic size difference of the solid-solution formed in as-milled HEA powders is broader.Moreover,the variation ranges between mixing enthalpy and entropy with atomic size difference of the amorphous phase in HEA powder become wider than those of high-entropy bulk metallic glass.展开更多
基金financial supports from the National Natural Science Foundation of China (No.51971102)the Major Basic Research Projects of Shandong Natural Science Foundation,China (No.ZR2020ZD06)+1 种基金the Open Research Fund of Songshan Lake Materials Laboratory,China (No.2021SLABFK08)the Science and Technology Program of University of Jinan,China (No.XKY2117)。
文摘The alloying behavior and microstructures of the(CoCrFeNiMn)_(90)M_(10)(M=Al,Hf)high-entropy alloy(HEA)powders fabricated by mechanical alloying were studied.The CoCrFeNiMn)_(90)Al_(10) powders have duplex solid-solution structures.In contrast,nanocrystalline HfNi_(3) anchoring in amorphous structures is found in the(CoCrFeNiMn)_(90)Hf_(10) powders.The(CoCrFeNiMn)_(90)Al_(10) powders show better ferromagnetic behaviors,mainly explained by the facilitated motion of the magnetic domain induced by the coherent interface between duplex phases.Combined with our previous work,the rules of forming solid-solution and amorphous phase in as-milled HEA powders are preliminarily proposed.It is found that,compared with the as-cast HEA reported previously,the variation range of mixing enthalpy with atomic size difference of the solid-solution formed in as-milled HEA powders is broader.Moreover,the variation ranges between mixing enthalpy and entropy with atomic size difference of the amorphous phase in HEA powder become wider than those of high-entropy bulk metallic glass.