The corrosion behavior of 316H stainless steel(SS)in the impure and purified Na Cl–KCl–Mg Cl_(2) salt was investigated at700°C.Results indicate that the main deleterious impurity induced corrosion in the impure...The corrosion behavior of 316H stainless steel(SS)in the impure and purified Na Cl–KCl–Mg Cl_(2) salt was investigated at700°C.Results indicate that the main deleterious impurity induced corrosion in the impure salt was the absorbed moisture,present in the form of Mg Cl_(2)·6H_(2)O.316H SS occurred severe intergranular corrosion with a corrosion depth of 130μm for1000 h in the impure Na Cl–KCl–Mg Cl_(2) salt.In contrast,the purification treatment of molten chloride salt by the dissolved Mg metal can remove the absorbed moisture,and the corresponding reactions were also discussed.As a result,the corrosiveness of Na Cl–KCl–Mg Cl_(2) salt is reduced significantly.316H SS occurred slight uniform corrosion with a depth of less than 5μm for 3000 h in the purified Na Cl–KCl–Mg Cl_(2) salt.展开更多
基金supported by the National Science Foundation of Shanghai(No.22ZR1474600)the National Natural Science Foundation of China(No.12175302)+1 种基金the“Thorium Molten Salt Reactor Nuclear Energy System”Strategic Priority Research Program of the Chinese Academy of Sciences(No.XDA 02040000)the“Transformational Technologies for Clean Energy and Demonstration,”Strategic Priority Research Program of the Chinese Academy of Sciences(No.XDA 21000000)。
文摘The corrosion behavior of 316H stainless steel(SS)in the impure and purified Na Cl–KCl–Mg Cl_(2) salt was investigated at700°C.Results indicate that the main deleterious impurity induced corrosion in the impure salt was the absorbed moisture,present in the form of Mg Cl_(2)·6H_(2)O.316H SS occurred severe intergranular corrosion with a corrosion depth of 130μm for1000 h in the impure Na Cl–KCl–Mg Cl_(2) salt.In contrast,the purification treatment of molten chloride salt by the dissolved Mg metal can remove the absorbed moisture,and the corresponding reactions were also discussed.As a result,the corrosiveness of Na Cl–KCl–Mg Cl_(2) salt is reduced significantly.316H SS occurred slight uniform corrosion with a depth of less than 5μm for 3000 h in the purified Na Cl–KCl–Mg Cl_(2) salt.