The dephosphorization experiments of low phosphorus containing steel by CaO-based and BaO-based fluxes were carried out. The effects of the oxygen potential in molten steel and the BaO content in the slag on dephospho...The dephosphorization experiments of low phosphorus containing steel by CaO-based and BaO-based fluxes were carried out. The effects of the oxygen potential in molten steel and the BaO content in the slag on dephosphorization and rephosphorization of molten steel were analyzed. The results showed that the dephosphorization ratio of more than 50% and the ultra-low phosphorus content of less than 0.005% in steel were obtained by the three kinds of dephosphorization fluxes as the oxygen potential of molten steel higher than 400×10^-6. Rephosphorization of molten steel was serious as the oxygen content of molten steel lower than 10×10^-6. BaO-based fluxes can improve the dephosphorization effect and reduce the phosphorus pick-up effectively under the condition of weak deoxidization of molten steel （the oxygen potential is about 100×10^-6）, but can not prevent rephosphorization under the condition of deep deoxidization of molten steel （the oxygen potential less than 10×10^-6）.展开更多
The fact that the amount of the mold flux components differs at differentlocations on the cracking surface indicates that the longitudinal surface cracks are initiallyformed in the mold and are enlarged in the seconda...The fact that the amount of the mold flux components differs at differentlocations on the cracking surface indicates that the longitudinal surface cracks are initiallyformed in the mold and are enlarged in the secondary cooling zone. Based on the hot ductilitymeasurement of two typical container used steels, it is known that the steels are in severeembrittlement state in the temperature range of 825-775 deg C. By means of increasing Cr/Ni platingthickness on the upper part of the mold, reducing mold heat flux, adopting new secondary coolingpattern, etc., the occurrence of the surface longitudinal cracks on the steel CC (continuouscasting) slabs has been significantly reduced.展开更多
The desulfurization experiment of an Al2O3-CaO base pre-molten refining slag containing SrO was carried out. Experimental samples were made from industrial materials. In order to predict the slag's desulfurization...The desulfurization experiment of an Al2O3-CaO base pre-molten refining slag containing SrO was carried out. Experimental samples were made from industrial materials. In order to predict the slag's desulfurization ability, sulphur capacity was calculated by means of optical basicity, and there is consistency between calculated results and experimental data. A mathematical model between components and sulphur partition ratio was established with the experimental data. Based on the regression equation, the effects of single and interactive components on sulphur partition ratio were discussed. The results show that the sulphur capacity and distribution ratio decrease with the increment of Al2O3/CaO. SrO and MgO can increase the sulphur partition ratio. The best content of SrO in the slag should not be more than 10%, and the MgO content should be about 8%. The effect of CaF2 on sulphur partition ratio is not obvious, therefore the addition should be limited for environmental protection.展开更多
The effect of [S] on strength and toughness of low alloy steel plates inwhich sum of [P], [N], T[O] is less than 8x10^(-5) and the effect of T[O] on strength and toughnessof the steel plates in which sum of [S], [P], ...The effect of [S] on strength and toughness of low alloy steel plates inwhich sum of [P], [N], T[O] is less than 8x10^(-5) and the effect of T[O] on strength and toughnessof the steel plates in which sum of [S], [P], [N] is less than 7x10^(-5) were investigated. It isfound that the strength of the steel plates decreases with increasing [S] content when [S] is lessthan 4x10^(-5). When [S] varies within the range of 4x10^(-5)-1.2x10^(-4), [S] has no significanteffect on strength of the steel. The strength of the steel plates increases with increasing T[O]content when T[O] is less than 30x10^(-6), but decreases with increasing T[O] when T[O] is more than3x10^(-5). The difference between the LETT in plate length direction and LETT in width directiondecreases with decreasing [S] content. However, even when [S] is decreased to 9x10^(-6), thedifference of the LETT is still 16℃. When T[O] varies between 1.8x10^(-5) and 5.2x10^(-5), the lowtemperature impact toughness of the steel plates slowly decreases with T[O] increasing. When T[O]increases to more than 5.2x10^(-5), the low temperature toughness of the steel rapidly decreaseswith increasing T[O] content.展开更多
The hot ductility of the V-containing micro-alloying steel CC (continuouscasting) slabs and precipitation of vanadium carbide in the tensile specimens were investigated. Theresults indicate that the precipitation rati...The hot ductility of the V-containing micro-alloying steel CC (continuouscasting) slabs and precipitation of vanadium carbide in the tensile specimens were investigated. Theresults indicate that the precipitation ratio and precipitation rate of vanadium in the specimensreach maximum respectively at 900, -825 and 825 deg C. There is still l0 percent-l7 percent ofvanadium precipitated when the deformation temperature decreases to 800-700 deg C. Vanadium largelyaffects the ductility of the steel in the low ductility temperature Region III. Embrittlement ofsteel with higher V content is severer in the region and the embrittlement extends to lowertemperature.展开更多
文摘The dephosphorization experiments of low phosphorus containing steel by CaO-based and BaO-based fluxes were carried out. The effects of the oxygen potential in molten steel and the BaO content in the slag on dephosphorization and rephosphorization of molten steel were analyzed. The results showed that the dephosphorization ratio of more than 50% and the ultra-low phosphorus content of less than 0.005% in steel were obtained by the three kinds of dephosphorization fluxes as the oxygen potential of molten steel higher than 400×10^-6. Rephosphorization of molten steel was serious as the oxygen content of molten steel lower than 10×10^-6. BaO-based fluxes can improve the dephosphorization effect and reduce the phosphorus pick-up effectively under the condition of weak deoxidization of molten steel （the oxygen potential is about 100×10^-6）, but can not prevent rephosphorization under the condition of deep deoxidization of molten steel （the oxygen potential less than 10×10^-6）.
文摘The fact that the amount of the mold flux components differs at differentlocations on the cracking surface indicates that the longitudinal surface cracks are initiallyformed in the mold and are enlarged in the secondary cooling zone. Based on the hot ductilitymeasurement of two typical container used steels, it is known that the steels are in severeembrittlement state in the temperature range of 825-775 deg C. By means of increasing Cr/Ni platingthickness on the upper part of the mold, reducing mold heat flux, adopting new secondary coolingpattern, etc., the occurrence of the surface longitudinal cracks on the steel CC (continuouscasting) slabs has been significantly reduced.
文摘The desulfurization experiment of an Al2O3-CaO base pre-molten refining slag containing SrO was carried out. Experimental samples were made from industrial materials. In order to predict the slag's desulfurization ability, sulphur capacity was calculated by means of optical basicity, and there is consistency between calculated results and experimental data. A mathematical model between components and sulphur partition ratio was established with the experimental data. Based on the regression equation, the effects of single and interactive components on sulphur partition ratio were discussed. The results show that the sulphur capacity and distribution ratio decrease with the increment of Al2O3/CaO. SrO and MgO can increase the sulphur partition ratio. The best content of SrO in the slag should not be more than 10%, and the MgO content should be about 8%. The effect of CaF2 on sulphur partition ratio is not obvious, therefore the addition should be limited for environmental protection.
基金This research was supported by the State Key Fundamental Research Project (973 Project), (No. G199806150)
文摘The effect of [S] on strength and toughness of low alloy steel plates inwhich sum of [P], [N], T[O] is less than 8x10^(-5) and the effect of T[O] on strength and toughnessof the steel plates in which sum of [S], [P], [N] is less than 7x10^(-5) were investigated. It isfound that the strength of the steel plates decreases with increasing [S] content when [S] is lessthan 4x10^(-5). When [S] varies within the range of 4x10^(-5)-1.2x10^(-4), [S] has no significanteffect on strength of the steel. The strength of the steel plates increases with increasing T[O]content when T[O] is less than 30x10^(-6), but decreases with increasing T[O] when T[O] is more than3x10^(-5). The difference between the LETT in plate length direction and LETT in width directiondecreases with decreasing [S] content. However, even when [S] is decreased to 9x10^(-6), thedifference of the LETT is still 16℃. When T[O] varies between 1.8x10^(-5) and 5.2x10^(-5), the lowtemperature impact toughness of the steel plates slowly decreases with T[O] increasing. When T[O]increases to more than 5.2x10^(-5), the low temperature toughness of the steel rapidly decreaseswith increasing T[O] content.
文摘The hot ductility of the V-containing micro-alloying steel CC (continuouscasting) slabs and precipitation of vanadium carbide in the tensile specimens were investigated. Theresults indicate that the precipitation ratio and precipitation rate of vanadium in the specimensreach maximum respectively at 900, -825 and 825 deg C. There is still l0 percent-l7 percent ofvanadium precipitated when the deformation temperature decreases to 800-700 deg C. Vanadium largelyaffects the ductility of the steel in the low ductility temperature Region III. Embrittlement ofsteel with higher V content is severer in the region and the embrittlement extends to lowertemperature.