Titanium silicate-1(TS-1) was treated with a mixed alkaline of tetrapropyl ammonium hydroxide(TPAOH) and NaOH. It was characterized by XRD, nitrogen physical adsorption, SEM, FT-IR, UV-Vis and ICPOES, and studied in p...Titanium silicate-1(TS-1) was treated with a mixed alkaline of tetrapropyl ammonium hydroxide(TPAOH) and NaOH. It was characterized by XRD, nitrogen physical adsorption, SEM, FT-IR, UV-Vis and ICPOES, and studied in propylene epoxidation. The mixed alkaline treatment with TPAOH/NaOH solution did not destroy the MFI structure of TS-1. With increasing NaOH concentrations, the relative crystallinity and the framework titanium decreased to some extent while the mesopore volume, mesopore diameter, and extra-framework titanium increased appreciably. When NaOH concentration was 0.0333 mol L^(-1), the best catalytic performance was obtained.展开更多
TS-1/SiO_2 extrudate was post-treated with mixed solution of tetrapropyl ammonium hydroxide(TPAOH)and various ammonium salts solution(NH_4F,(NH_4)_3PO_4,(NH_4)_2CO_3,(NH_4)_2SO_4,NH_4CH_3CO_2,NH_4NO_3,NH_4Cl and(NH_4)...TS-1/SiO_2 extrudate was post-treated with mixed solution of tetrapropyl ammonium hydroxide(TPAOH)and various ammonium salts solution(NH_4F,(NH_4)_3PO_4,(NH_4)_2CO_3,(NH_4)_2SO_4,NH_4CH_3CO_2,NH_4NO_3,NH_4Cl and(NH_4)_2TiF_6).The obtained hierarchical TS-1 catalysts were characterized by many techniques and tested for propylene epoxidation using hydrogen peroxide as an oxidant in a fixed-bed reactor.It was shown that the physicochemical and catalytic properties of the treated TS-1/SiO_2 extrudate depended on the types of ammonium salts added.Compared to the treatment with TPAOH alone,the treatment with a mixed solution of TPAOH and some ammonium salts can greatly improve the catalytic properties of the treated TS-1/SiO_2 extrudate.Some of these ammonium salts were favorable for the incorporation of titanium in the framework,and the beneficial effect depended on the types of ammonium salt.TS-1/SiO_2 extrudate treated with a mixed solution of TPAOH and(NH_4)_3PO_4 exhibited the highest catalyst stability in propylene epoxidation.Such catalytic property can be correlated to high crystallinity,more framework titanium,large specific surface area and large external surface area.展开更多
基金supported by the National Natural Science Foundation of China (No.21276183)
文摘Titanium silicate-1(TS-1) was treated with a mixed alkaline of tetrapropyl ammonium hydroxide(TPAOH) and NaOH. It was characterized by XRD, nitrogen physical adsorption, SEM, FT-IR, UV-Vis and ICPOES, and studied in propylene epoxidation. The mixed alkaline treatment with TPAOH/NaOH solution did not destroy the MFI structure of TS-1. With increasing NaOH concentrations, the relative crystallinity and the framework titanium decreased to some extent while the mesopore volume, mesopore diameter, and extra-framework titanium increased appreciably. When NaOH concentration was 0.0333 mol L^(-1), the best catalytic performance was obtained.
基金supported by National Natural Science Foundation of China (No. 21276183)
文摘TS-1/SiO_2 extrudate was post-treated with mixed solution of tetrapropyl ammonium hydroxide(TPAOH)and various ammonium salts solution(NH_4F,(NH_4)_3PO_4,(NH_4)_2CO_3,(NH_4)_2SO_4,NH_4CH_3CO_2,NH_4NO_3,NH_4Cl and(NH_4)_2TiF_6).The obtained hierarchical TS-1 catalysts were characterized by many techniques and tested for propylene epoxidation using hydrogen peroxide as an oxidant in a fixed-bed reactor.It was shown that the physicochemical and catalytic properties of the treated TS-1/SiO_2 extrudate depended on the types of ammonium salts added.Compared to the treatment with TPAOH alone,the treatment with a mixed solution of TPAOH and some ammonium salts can greatly improve the catalytic properties of the treated TS-1/SiO_2 extrudate.Some of these ammonium salts were favorable for the incorporation of titanium in the framework,and the beneficial effect depended on the types of ammonium salt.TS-1/SiO_2 extrudate treated with a mixed solution of TPAOH and(NH_4)_3PO_4 exhibited the highest catalyst stability in propylene epoxidation.Such catalytic property can be correlated to high crystallinity,more framework titanium,large specific surface area and large external surface area.