采用激光-MAG(Metal active gas arc welding)复合焊接工艺,以焊缝表面成形、焊缝纵截面形貌和熔深波动程度为工艺稳定性评价依据,借助高速摄像系统和图像处理方法,对焊接过程中飞溅和等离子体两种关键过程信息进行特征识别和定量化表征...采用激光-MAG(Metal active gas arc welding)复合焊接工艺,以焊缝表面成形、焊缝纵截面形貌和熔深波动程度为工艺稳定性评价依据,借助高速摄像系统和图像处理方法,对焊接过程中飞溅和等离子体两种关键过程信息进行特征识别和定量化表征,系统地研究激光功率从5 kW提高到30 kW时,焊接过程关键特征信息与焊接过程稳定性之间的关系。结果表明,随着激光功率的增加,焊缝表面成形出现周期性“上凸-下凹”现象,焊缝内部裂纹和熔深变化特征也随之周期性变化;等离子体面积和飞溅面积均随激光功率的提高呈增加趋势,且两者波动程度和熔深波动程度均呈正相关;等离子体面积增加会导致激光传输过程中能量衰减程度的加剧,使焊缝熔深增加趋势逐渐变缓,其波动程度是影响焊接过程稳定性的关键因素之一。展开更多
Welding research of A6N01S-T5 aluminum alloy profile for high-speed train was done by using laser-MIG hybrid welding and MIG welding individually. And the weld appearance,welding distortion,mechanical properties of th...Welding research of A6N01S-T5 aluminum alloy profile for high-speed train was done by using laser-MIG hybrid welding and MIG welding individually. And the weld appearance,welding distortion,mechanical properties of the joints and microstructures were analyzed. The test results demonstrated that high-efficient welding for the profile can be achieved by using laser-MIG hybrid welding,the speed of which can be over 3. 0 m/min. The processing had a good gap bridging ability,even if the gap of the butt joint was up to 2. 0 mm,a good weld appearance can also be got. While the hybrid welding speed was greater than 2. 5 m/min,the welding distortion of the laser-tandem MIG hybrid joints was just about 33% of that of the MIG joints,but the welding efficiency was over 3 times of MIG welding. And tensile strength of the hybrid joints was 85% of that of A6N01S-T5 base metal,9% higher than that of the MIG joints. Fatigue properties was tested individually with pulsed tensile fatigue method in the condition of 1 × 10~7 lifetime. The test results demonstrated that the fatigue strength of the joints was a little lower than that of base material,which could be up to 115 MPa. But the fatigue strength of hybrid welding joints was 107. 5 MPa,which was 23% higher than 87 MPa of MIG welding joints.展开更多
Based on the pulsed plasma arc welding(PPAW),a rapid remanufacturing shaping system,including a structured light scanning reverse engineering(RE)system,a robot system and a PPAW source system have been developed.The n...Based on the pulsed plasma arc welding(PPAW),a rapid remanufacturing shaping system,including a structured light scanning reverse engineering(RE)system,a robot system and a PPAW source system have been developed.The new rapid remanufacturing shaping system can rapidly and accurately repair the worn parts with different damaged degrees and thus extend their life cycle.In the present paper,the whole process of repairing worn parts is described.Firstly,the scanning model of a worn part is obtained by using RE system based on reconstructing approach.Compared with standard CAD model in the undamaged setting,the surface profile and the extent of damage area are obtained.Secondly,the weld repair path is designed by slicing the point cloud model of damage area.This path consists of multilayer parallel lines that produce parallel overlapped weld beads which cover the damaged area.By off-line programming techniques,the robot executable program as document format is transmitted to the robot controller for repairing worn parts.Finally,the weld repair experiments on worn steel plane plate and damaged column are performed to evaluate the remanufacturing system.展开更多
文摘采用激光-MAG(Metal active gas arc welding)复合焊接工艺,以焊缝表面成形、焊缝纵截面形貌和熔深波动程度为工艺稳定性评价依据,借助高速摄像系统和图像处理方法,对焊接过程中飞溅和等离子体两种关键过程信息进行特征识别和定量化表征,系统地研究激光功率从5 kW提高到30 kW时,焊接过程关键特征信息与焊接过程稳定性之间的关系。结果表明,随着激光功率的增加,焊缝表面成形出现周期性“上凸-下凹”现象,焊缝内部裂纹和熔深变化特征也随之周期性变化;等离子体面积和飞溅面积均随激光功率的提高呈增加趋势,且两者波动程度和熔深波动程度均呈正相关;等离子体面积增加会导致激光传输过程中能量衰减程度的加剧,使焊缝熔深增加趋势逐渐变缓,其波动程度是影响焊接过程稳定性的关键因素之一。
基金supported by National Natural Science Foundation of China(61640423)Additive Manufacturing&Laser Manufacturing of China(2016YFB1102100)High-end CNC Machine Tools&Basic Manufacturing Equipment of China(2016ZX04003002)
文摘Welding research of A6N01S-T5 aluminum alloy profile for high-speed train was done by using laser-MIG hybrid welding and MIG welding individually. And the weld appearance,welding distortion,mechanical properties of the joints and microstructures were analyzed. The test results demonstrated that high-efficient welding for the profile can be achieved by using laser-MIG hybrid welding,the speed of which can be over 3. 0 m/min. The processing had a good gap bridging ability,even if the gap of the butt joint was up to 2. 0 mm,a good weld appearance can also be got. While the hybrid welding speed was greater than 2. 5 m/min,the welding distortion of the laser-tandem MIG hybrid joints was just about 33% of that of the MIG joints,but the welding efficiency was over 3 times of MIG welding. And tensile strength of the hybrid joints was 85% of that of A6N01S-T5 base metal,9% higher than that of the MIG joints. Fatigue properties was tested individually with pulsed tensile fatigue method in the condition of 1 × 10~7 lifetime. The test results demonstrated that the fatigue strength of the joints was a little lower than that of base material,which could be up to 115 MPa. But the fatigue strength of hybrid welding joints was 107. 5 MPa,which was 23% higher than 87 MPa of MIG welding joints.
文摘Based on the pulsed plasma arc welding(PPAW),a rapid remanufacturing shaping system,including a structured light scanning reverse engineering(RE)system,a robot system and a PPAW source system have been developed.The new rapid remanufacturing shaping system can rapidly and accurately repair the worn parts with different damaged degrees and thus extend their life cycle.In the present paper,the whole process of repairing worn parts is described.Firstly,the scanning model of a worn part is obtained by using RE system based on reconstructing approach.Compared with standard CAD model in the undamaged setting,the surface profile and the extent of damage area are obtained.Secondly,the weld repair path is designed by slicing the point cloud model of damage area.This path consists of multilayer parallel lines that produce parallel overlapped weld beads which cover the damaged area.By off-line programming techniques,the robot executable program as document format is transmitted to the robot controller for repairing worn parts.Finally,the weld repair experiments on worn steel plane plate and damaged column are performed to evaluate the remanufacturing system.