In order to analyze the effect of scratch on the corrosion behaviour of a calcium phosphate conversion coating(CPCC)on AZ80,the electrochemical testing,scanning vibrating electrode technique(SVET),immersion test and h...In order to analyze the effect of scratch on the corrosion behaviour of a calcium phosphate conversion coating(CPCC)on AZ80,the electrochemical testing,scanning vibrating electrode technique(SVET),immersion test and hydrogen evolution experiment were performed to study the corrosion resistance of AZ80,AZ80 with CPCC and coated AZ80 with scratch.The results show that the coating improves the corrosion resistance of the AZ80 from a current density of(85±4)to(4±1)μA/cm^(2).When the coating was damaged,its protection on substrate would be reduced.The scratch with a length of around 12 mm on the coating reduced the corrosion resistance to a current density of(39±1)μA/cm^(2).In addition,the corrosion occurred initially in the scratch area and the corrosion site first occurred at the junction of the scratch and the coating.Besides,the micro corrosion mechanism of the specimen containing scratch was clarified.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.52071036,51701027)the Fundamental Research Funds for the Central Universities,China(Nos.2020CDJQY-A002,2021CDJCGJ009)the National Key Research and Development Program of China(Nos.2016YFB0301100,2016YFB0101700)。
文摘In order to analyze the effect of scratch on the corrosion behaviour of a calcium phosphate conversion coating(CPCC)on AZ80,the electrochemical testing,scanning vibrating electrode technique(SVET),immersion test and hydrogen evolution experiment were performed to study the corrosion resistance of AZ80,AZ80 with CPCC and coated AZ80 with scratch.The results show that the coating improves the corrosion resistance of the AZ80 from a current density of(85±4)to(4±1)μA/cm^(2).When the coating was damaged,its protection on substrate would be reduced.The scratch with a length of around 12 mm on the coating reduced the corrosion resistance to a current density of(39±1)μA/cm^(2).In addition,the corrosion occurred initially in the scratch area and the corrosion site first occurred at the junction of the scratch and the coating.Besides,the micro corrosion mechanism of the specimen containing scratch was clarified.