A series of new double perovskite LaEuCaSnO(0≤x≤0.8)red phosphors were synthesized by traditional solid-state reaction.The phase,micro structure,photoluminescence(PL)properties,quantum efficiency,and thermal stabili...A series of new double perovskite LaEuCaSnO(0≤x≤0.8)red phosphors were synthesized by traditional solid-state reaction.The phase,micro structure,photoluminescence(PL)properties,quantum efficiency,and thermal stability of the phosphors were investigated.LaCaSnOmatrix has a monoclinic double perovskite structure with space group P2/n.Under near-ultraviolet(UV)light at395 nm,LaEuCaSnOphosphors exhibit the most typical red emission peak at 614 nm,which corresponds to~5 D→~7 Felectric dipole transition of Eu.The optimum Eudoping content is attained at x=0.5,and the LaEuCaSnOphosphor shows a moderate quantum efficiency(32.3%)and high color purity(92.2%).Besides,the temperature-dependent spectrum of the phosphor was studied.The emission intensity of Euat 423 K decreases to 70.94%of the initial intensity at 303 K,and the activation energyΔE is estimated to be 0.232 eV,suggesting that the phosphors possess good thermal stability.The fabricated w-LED based on the phosphors has higher Ra(89),lower CCT(4539 K),and better chromaticity coo rdinates(0.371,0.428).These results prove that the Eu-doped LaCaSnOred phosphor has great potential applications in w-LEDs.展开更多
基金Project supported by the National Natural Science Foundation of China(61974114)。
文摘A series of new double perovskite LaEuCaSnO(0≤x≤0.8)red phosphors were synthesized by traditional solid-state reaction.The phase,micro structure,photoluminescence(PL)properties,quantum efficiency,and thermal stability of the phosphors were investigated.LaCaSnOmatrix has a monoclinic double perovskite structure with space group P2/n.Under near-ultraviolet(UV)light at395 nm,LaEuCaSnOphosphors exhibit the most typical red emission peak at 614 nm,which corresponds to~5 D→~7 Felectric dipole transition of Eu.The optimum Eudoping content is attained at x=0.5,and the LaEuCaSnOphosphor shows a moderate quantum efficiency(32.3%)and high color purity(92.2%).Besides,the temperature-dependent spectrum of the phosphor was studied.The emission intensity of Euat 423 K decreases to 70.94%of the initial intensity at 303 K,and the activation energyΔE is estimated to be 0.232 eV,suggesting that the phosphors possess good thermal stability.The fabricated w-LED based on the phosphors has higher Ra(89),lower CCT(4539 K),and better chromaticity coo rdinates(0.371,0.428).These results prove that the Eu-doped LaCaSnOred phosphor has great potential applications in w-LEDs.