Principle of multilayer spray forming and preparation technique of tubes and billets by it were presented and described in the article. The marked characteristic of multilayer spray forming technology is the to and fr...Principle of multilayer spray forming and preparation technique of tubes and billets by it were presented and described in the article. The marked characteristic of multilayer spray forming technology is the to and fro movement of spray system, so the preform is deposited layer by layer with the surface of the deposit retaining relatively low temperature during the spray forming process. The two outstanding advantages of multilayer spray forming are as follows: suitable for manufacturing large dimension blanks, higher solidification cooling rate. Now Al Fe V Si alloy (8009) and SiC particle reinforced aluminium alloy metal matrix composite billets of 300 600 mm in diameter and tubular blanks of size up to 650 mm in outer diameter, 360 mm in inner diameter and 1 200 mm in length have been made with the technology. After extrusion, the material has good properties.展开更多
文摘Principle of multilayer spray forming and preparation technique of tubes and billets by it were presented and described in the article. The marked characteristic of multilayer spray forming technology is the to and fro movement of spray system, so the preform is deposited layer by layer with the surface of the deposit retaining relatively low temperature during the spray forming process. The two outstanding advantages of multilayer spray forming are as follows: suitable for manufacturing large dimension blanks, higher solidification cooling rate. Now Al Fe V Si alloy (8009) and SiC particle reinforced aluminium alloy metal matrix composite billets of 300 600 mm in diameter and tubular blanks of size up to 650 mm in outer diameter, 360 mm in inner diameter and 1 200 mm in length have been made with the technology. After extrusion, the material has good properties.