Polyvinylidene fluoride(PVDF)/polyurethane(PU)composite nanofiber membranes were prepared by mixing PVDF and PU at different mass ratios.The microstructure and the crystal structure of the composite nanofiber membrane...Polyvinylidene fluoride(PVDF)/polyurethane(PU)composite nanofiber membranes were prepared by mixing PVDF and PU at different mass ratios.The microstructure and the crystal structure of the composite nanofiber membranes were analyzed by scanning electron microscopy(SEM),Fourier transform infrared(FTIR)spectroscopy and X-ray diffraction(XRD).The hydrophilicity,mechanical properties and piezoelectric properties were also tested.Results showed that when the mass ratio of PVDF to PU was 9∶1,the fiber membrane had the best microstructure,and the crystal form of PVDF changed fromαcrystal toβcrystal in the electrospinning.The addition of PU improved the hydrophilicity,mechanical properties,and piezoelectric signal of the fiber membrane.When the mass ratio of PVDF to PU was 9∶1,the tensile strength reached the peak value of(10.39±0.41)N,and the output voltage reached the maximum value of(1.98±0.12)V.展开更多
基金Natural Science Foundation of Jiangsu Province,China(No.BK20190927)Postdoctoral Daily Program of Jiangsu Province,China(No.2019Z104)+2 种基金Natural Science Research Project of Xinglin College of Nantong University,China(No.2016K123)Student Innovation Training Project of Nantong University,China(No.2019111)Nantong University Scientific Research Fund,China(No.17R19)
文摘Polyvinylidene fluoride(PVDF)/polyurethane(PU)composite nanofiber membranes were prepared by mixing PVDF and PU at different mass ratios.The microstructure and the crystal structure of the composite nanofiber membranes were analyzed by scanning electron microscopy(SEM),Fourier transform infrared(FTIR)spectroscopy and X-ray diffraction(XRD).The hydrophilicity,mechanical properties and piezoelectric properties were also tested.Results showed that when the mass ratio of PVDF to PU was 9∶1,the fiber membrane had the best microstructure,and the crystal form of PVDF changed fromαcrystal toβcrystal in the electrospinning.The addition of PU improved the hydrophilicity,mechanical properties,and piezoelectric signal of the fiber membrane.When the mass ratio of PVDF to PU was 9∶1,the tensile strength reached the peak value of(10.39±0.41)N,and the output voltage reached the maximum value of(1.98±0.12)V.