Introduction:Chemokine-like factor 1(CKLF1)is a chemokine that is overexpressed in several diseases.Our previousfindings revealed a significant increase in CKLF1 expression in the ischemic brain,suggesting its potential as a therapeutic target for ischemic stroke.Methods:In this study,we examined the expression dynamics of CKLF1 in both in vivo and in vitro models of ischemic cardiac injury.Myocardial infarction(MI)was induced in vivo by ligation of the left anterior descending artery(LAD)of the rat heart.The levels of CKLF1,Creatine Kinase MB Isoenzyme(CK-MB),and Lactate dehydrogenase(LDH)in the serum were detected using Enzyme-linked immunosorbent assay(ELISA).The expression of CKLF1 in the infarcted area was detected by immunohistochemistry,immunofluorescence,quantitative PCR(qPCR),and Western blotting(WB).H9C2 and AC16 cardiomyocytes cultured in vitro were subjected to oxygen and glucose deprivation(OGD).LDH was used to detect cell damage,and CKLF1 expression was detected by qPCR and WB.Results:CKLF1 mRNA and protein expression were significantly increased in h9c2 cells at 1.5 h and in AC16 cells at 4 h after OGD.The serum CK-MB in rats increased significantly on thefirst day after infarction,while the LDH concentration increased significantly on the third day after infarction.CKLF1 blood levels significantly increased on thefirst day following MI in rats.CKLF1 expression notably increased in the infarct area on days 1,3,and 7 post-MI.In MI tissue,CKLF1 colocalizes with cardiomyocytes,macrophages,and neutrophils.Conclusion:CKLF1 was substantially expressed during myocardial ischemia injury both in vivo and in vitro and was colocalized with macrophages and neutrophils,indicating that CKLF1 is expected to be a biomarker and a drug target for the treatment of myocardial infarction.

Improving fatigue strength of bainite/martensite dual-phase steels in very high cycle fatigue regime by refining microstructures

Very high cycle fatigue behaviors of two bainite/martensite dual-phase steels were investigated.One of the steels was cyclic rapid heat treated and its microstructures were refined. Fatigue strength of the steel is 225 MPa higher than that without refining.Observation of fracture surfaces show that the fatigue cracks initiate at bainites for non-refined steel and at non-metallic inclusions for the refined steel.The size of inclusions is much smaller than that of bainites which results in the improvement of fatigue strength.