Laser surface remelting of medium Ni-Cr infinite chilling cast iron was performed with a continuous wave COa laser beam with the power of 7 KW under the argon shielding. The microstructural analysis of the laser remel...Laser surface remelting of medium Ni-Cr infinite chilling cast iron was performed with a continuous wave COa laser beam with the power of 7 KW under the argon shielding. The microstructural analysis of the laser remelted layer by optical microscope shows that the laser remelted layer consists of three zones, which is the melting zone, the transition zone and the heat affected zone. The size of the dendrite of the melting zone is only in the 1/10 to 1/30 range of that of the substrate. The distribution of the hardness of the laser remelted layer was detected, and the carrying capacity of rolling steel was also field-tested. The results show that both the hardness of the remelted layer and the carrying capacity all increase, especially, the carrying capacity was 50% increased compared with the substrate.展开更多
文摘Laser surface remelting of medium Ni-Cr infinite chilling cast iron was performed with a continuous wave COa laser beam with the power of 7 KW under the argon shielding. The microstructural analysis of the laser remelted layer by optical microscope shows that the laser remelted layer consists of three zones, which is the melting zone, the transition zone and the heat affected zone. The size of the dendrite of the melting zone is only in the 1/10 to 1/30 range of that of the substrate. The distribution of the hardness of the laser remelted layer was detected, and the carrying capacity of rolling steel was also field-tested. The results show that both the hardness of the remelted layer and the carrying capacity all increase, especially, the carrying capacity was 50% increased compared with the substrate.