Glass formation, mechanical and magnetic properties of the Fe76-xC7.0Si3.3B5.0P8.7Mox (x=0, 1 at.%, 3 at.% and 5 at.%) alloys prepared using an industrial Fe-P master alloy have been studied. With the substitution of ...Glass formation, mechanical and magnetic properties of the Fe76-xC7.0Si3.3B5.0P8.7Mox (x=0, 1 at.%, 3 at.% and 5 at.%) alloys prepared using an industrial Fe-P master alloy have been studied. With the substitution of Mo for Fe, glass-forming ability (GFA) was significantly enhanced and fully amorphous rods with a diameter of up to 5 mm were produced in the alloy with 3% Mo. The Mo-containing amorphous alloys also exhibited high fracture strength of 3635–3881 MPa and excellent magnetic properties including a high saturation magnetization of 1.10–1.41 T, a high Curie temperature and a low coercive force. The unique combination of high GFA, high fracture strength and excellent magnetic properties make the newly developed bulk metallic glasses viable for practical engineering applications.展开更多
基金supported by the National Natural Science Foundation of China (Grants Nos. 50725104 and 50841023)the National Basic Research Program of China (Grant No. 2007CB613903)China Post-doctoral Science Foundation (Grant No. 20080430019)
文摘Glass formation, mechanical and magnetic properties of the Fe76-xC7.0Si3.3B5.0P8.7Mox (x=0, 1 at.%, 3 at.% and 5 at.%) alloys prepared using an industrial Fe-P master alloy have been studied. With the substitution of Mo for Fe, glass-forming ability (GFA) was significantly enhanced and fully amorphous rods with a diameter of up to 5 mm were produced in the alloy with 3% Mo. The Mo-containing amorphous alloys also exhibited high fracture strength of 3635–3881 MPa and excellent magnetic properties including a high saturation magnetization of 1.10–1.41 T, a high Curie temperature and a low coercive force. The unique combination of high GFA, high fracture strength and excellent magnetic properties make the newly developed bulk metallic glasses viable for practical engineering applications.