To get a dielectric material with a high dielectric permittivity and suppressed dielectric loss,nano-Ag with a particle size of 20 nm and Ag@TiO_(2)core-shell particles with diameters of approximately 70-120 nm were e...To get a dielectric material with a high dielectric permittivity and suppressed dielectric loss,nano-Ag with a particle size of 20 nm and Ag@TiO_(2)core-shell particles with diameters of approximately 70-120 nm were embedded in polyvinylidene fluoride(PVDF)to fabricate nano-Ag/Ag@TiO_(2)/PVDF composites.After being modified by nano-Ag with 3 vol%optimal amount,the relative permittivity(ε_r)at 100 Hz of 50 vol%Ag@TiO_(2)/PVDF composites was 61,and the dielectric loss can be suppressed to 0.04,almost 96.4%lower than that of unmodified composites,and a higher frequency stability of bothε_r and loss has also been found.The underlying mechanism of the reduced loss was attributed to Maxwell-Wagner polarization and the Coulomb blockade effect caused by the introduction of a small amount of nano-Ag,which will block the movement of electrons between metal nanoparticles and composites.The space charge polarization and conductance loss are weakened at lower and higher Ag@TiO_(2)filling ratios,respectively,thus leading to a very low loss of the composites.展开更多
基金Funded by the National Natural Science Foundation of China(No.51772107)the Fundamental Research Funds for the Central Universities(No.2017KFYXJJ022)。
文摘To get a dielectric material with a high dielectric permittivity and suppressed dielectric loss,nano-Ag with a particle size of 20 nm and Ag@TiO_(2)core-shell particles with diameters of approximately 70-120 nm were embedded in polyvinylidene fluoride(PVDF)to fabricate nano-Ag/Ag@TiO_(2)/PVDF composites.After being modified by nano-Ag with 3 vol%optimal amount,the relative permittivity(ε_r)at 100 Hz of 50 vol%Ag@TiO_(2)/PVDF composites was 61,and the dielectric loss can be suppressed to 0.04,almost 96.4%lower than that of unmodified composites,and a higher frequency stability of bothε_r and loss has also been found.The underlying mechanism of the reduced loss was attributed to Maxwell-Wagner polarization and the Coulomb blockade effect caused by the introduction of a small amount of nano-Ag,which will block the movement of electrons between metal nanoparticles and composites.The space charge polarization and conductance loss are weakened at lower and higher Ag@TiO_(2)filling ratios,respectively,thus leading to a very low loss of the composites.