The study discussed the rapid method to test and predict the longevity of controlled release fertilizers （CRFs） coated by water soluble resin by using the short-term leaching under higher temperature. Pure water dis...The study discussed the rapid method to test and predict the longevity of controlled release fertilizers （CRFs） coated by water soluble resin by using the short-term leaching under higher temperature. Pure water dissolving incubation and higher temperature leaching were used to study the patterns of the nutrient release of the CRFs. The correlation analysis between the days at 25℃ and the hours at 80℃ of Trincote 1 and Trincote 2 for the same cumulative release rates were conducted. Patterns of cumulative nutrient release curve followed one factor quadratic regression equation at each given temperatures, and each of relative coefficient was bigger than 0.995. As the temperature increased, nutrients release of the CRFs increased. The longevity of resin coated CRFs were predicted by use of both the cumulative nutrients release equation at 80℃ and the regression equation of release time needed for the same cumulative release rates between 25 and 80℃. There were only 0.3-6.9% relative errors between the tested longevity and predicted one. In conclusion, the longevity of resin coated CRFs could be predicted more quickly and precisely by use of the higher temperature short-term leaching method than that of the traditional differential release rate. The longevity of resin coated CRF could be rapidly and precisely predicted in a few hours by application of the higher temperature shortterm leaching method.展开更多
基金the National Key Technologies R&D Program during the 11th Five-Year Plan period of China (2006BAD10B02)the National Natural Science Foundation of China (39870433,30270769)
文摘The study discussed the rapid method to test and predict the longevity of controlled release fertilizers （CRFs） coated by water soluble resin by using the short-term leaching under higher temperature. Pure water dissolving incubation and higher temperature leaching were used to study the patterns of the nutrient release of the CRFs. The correlation analysis between the days at 25℃ and the hours at 80℃ of Trincote 1 and Trincote 2 for the same cumulative release rates were conducted. Patterns of cumulative nutrient release curve followed one factor quadratic regression equation at each given temperatures, and each of relative coefficient was bigger than 0.995. As the temperature increased, nutrients release of the CRFs increased. The longevity of resin coated CRFs were predicted by use of both the cumulative nutrients release equation at 80℃ and the regression equation of release time needed for the same cumulative release rates between 25 and 80℃. There were only 0.3-6.9% relative errors between the tested longevity and predicted one. In conclusion, the longevity of resin coated CRFs could be predicted more quickly and precisely by use of the higher temperature short-term leaching method than that of the traditional differential release rate. The longevity of resin coated CRF could be rapidly and precisely predicted in a few hours by application of the higher temperature shortterm leaching method.