By means of an inherent elevated-temperature of poured liquid steel,a Ti-C-30wt%Fe preform,which was pre-placed in a mould cavity,was directly ignited and a combustion synthesis reaction took place.As a result,a TiC-F...By means of an inherent elevated-temperature of poured liquid steel,a Ti-C-30wt%Fe preform,which was pre-placed in a mould cavity,was directly ignited and a combustion synthesis reaction took place.As a result,a TiC-Fe cermet coating with a thickness of about 10mm was simultaneously synthesized on the solidified steel matrix.The synthesized coating exhibits a feature of graded composite structure,in which both the amount and size of TiC particles decrease gradually with an increasing distance from the furface of the coating.Moreover,by a proper casting technique,the pores formed during the combustion synthesis of the preform could be centrally distributed in 2-3mm in outer layer of the coating.When this outer porous layer was worn off,the rest coating with a thickness of about 8mm possesses a dense structure and a high abrasive wear resistance.展开更多
A new method is introduced to study the action between biomaterials and organism. By using an LKB- 2277 bioactivity monitor and ampoule method, the fundamental thermogenesis curves of the metabolic process of pk-15 an...A new method is introduced to study the action between biomaterials and organism. By using an LKB- 2277 bioactivity monitor and ampoule method, the fundamental thermogenesis curves of the metabolic process of pk-15 and the toxic effect of three kinds of selenomorpholine compounds on it were studied at 37℃. From the thermogenesis curves, the heat released by pk-15 metabolism was calculated. The results show that the selenium compounds all have toxic action on the metabolism process of pk-15 at the range of experimental concentrations. The sequence of the toxic action of selenium compounds is: Na2SeO3>β- ( N- selenomorpholine) -ethyl phenyike-tone hydrochloride > selenomorpholine.展开更多
The sintering resistance for conductive TiB2 and non-conductive A12O3 as well as empty die during pulse current sintering were investigated in this paper. Equivalent resistances were measured by current and valtage du...The sintering resistance for conductive TiB2 and non-conductive A12O3 as well as empty die during pulse current sintering were investigated in this paper. Equivalent resistances were measured by current and valtage during sintering the conductive and non-conductive materials in the same conditions. It is found that the current paths for conductive are different from those for non-conductive materials. For non-conductive materials, sintering resistances are influenced by powder sizes and heating rates, which indicates that pulse current has some interaction with non-conductive powders. For conductive TiB2 , sintering resistances are influenced by heating rates and ball-milling time, which indicates the effect of powders activated by spark.展开更多
基金FinanciallysupportedbytheNationalNaturalScienceFoundationofChina (No .5 0 2 76 0 2 3)
文摘By means of an inherent elevated-temperature of poured liquid steel,a Ti-C-30wt%Fe preform,which was pre-placed in a mould cavity,was directly ignited and a combustion synthesis reaction took place.As a result,a TiC-Fe cermet coating with a thickness of about 10mm was simultaneously synthesized on the solidified steel matrix.The synthesized coating exhibits a feature of graded composite structure,in which both the amount and size of TiC particles decrease gradually with an increasing distance from the furface of the coating.Moreover,by a proper casting technique,the pores formed during the combustion synthesis of the preform could be centrally distributed in 2-3mm in outer layer of the coating.When this outer porous layer was worn off,the rest coating with a thickness of about 8mm possesses a dense structure and a high abrasive wear resistance.
基金Funded by Natural Science Foundation of China (29973030 and 30170010)
文摘A new method is introduced to study the action between biomaterials and organism. By using an LKB- 2277 bioactivity monitor and ampoule method, the fundamental thermogenesis curves of the metabolic process of pk-15 and the toxic effect of three kinds of selenomorpholine compounds on it were studied at 37℃. From the thermogenesis curves, the heat released by pk-15 metabolism was calculated. The results show that the selenium compounds all have toxic action on the metabolism process of pk-15 at the range of experimental concentrations. The sequence of the toxic action of selenium compounds is: Na2SeO3>β- ( N- selenomorpholine) -ethyl phenyike-tone hydrochloride > selenomorpholine.
基金Supported by the Natural Science Foundation of China (59872024) Key Teacher Fund of National Education Ministry and Fund of State Key Lab of Plastic Forming Simulation and Die and Mould Technology(02 -11)
文摘The sintering resistance for conductive TiB2 and non-conductive A12O3 as well as empty die during pulse current sintering were investigated in this paper. Equivalent resistances were measured by current and valtage during sintering the conductive and non-conductive materials in the same conditions. It is found that the current paths for conductive are different from those for non-conductive materials. For non-conductive materials, sintering resistances are influenced by powder sizes and heating rates, which indicates that pulse current has some interaction with non-conductive powders. For conductive TiB2 , sintering resistances are influenced by heating rates and ball-milling time, which indicates the effect of powders activated by spark.