Cathode materials Li[CoxNiyMn1-x-y]O2 for lithium secondary batteries have been prepared by a new route using layered double hydroxides （LDHs） as a precursor. The resulting layered phase with the α- NaFe02 structur...Cathode materials Li[CoxNiyMn1-x-y]O2 for lithium secondary batteries have been prepared by a new route using layered double hydroxides （LDHs） as a precursor. The resulting layered phase with the α- NaFe02 structure crystallizes in the rhombohedral system, with space group R-3m having an interlayer spacing close to 0.47 nm. X-ray photoelectron spectroscopy （XPS） was used to measure the oxidation states of Co, Ni and Mn. The effects of varying the Co[Ni[Mn ratio on both the structure and electrochemical properties of Li[CoxNiyMn1-x-y]O2 have been investigated by X-ray diffraction and electrochemical tests. The products demonstrated a rather stable cycling behavior, with a reversible capacity of 118 mAh/g for the layered material with Co/Ni/Mn = 1/1/1.展开更多
基金supported by the National Natural Science Foun-dation of China, the 111 Project (grant no.: B07004) the Natural Science Foundation for Young Teachers of Beijing University of Chemical Technology (grant no.: QN0723)
文摘Cathode materials Li[CoxNiyMn1-x-y]O2 for lithium secondary batteries have been prepared by a new route using layered double hydroxides （LDHs） as a precursor. The resulting layered phase with the α- NaFe02 structure crystallizes in the rhombohedral system, with space group R-3m having an interlayer spacing close to 0.47 nm. X-ray photoelectron spectroscopy （XPS） was used to measure the oxidation states of Co, Ni and Mn. The effects of varying the Co[Ni[Mn ratio on both the structure and electrochemical properties of Li[CoxNiyMn1-x-y]O2 have been investigated by X-ray diffraction and electrochemical tests. The products demonstrated a rather stable cycling behavior, with a reversible capacity of 118 mAh/g for the layered material with Co/Ni/Mn = 1/1/1.