A new sol-gel process for the preparation of ultrafine nickel hydroxideelectrode materials was developed. The composite electrodes consisting of carbon nanotubes andNi(OH)_2 were developed by mixing the hydroxide and ...A new sol-gel process for the preparation of ultrafine nickel hydroxideelectrode materials was developed. The composite electrodes consisting of carbon nanotubes andNi(OH)_2 were developed by mixing the hydroxide and carbon nanotubes together in different massratios. In order to enhance energy density, a combined type pseudocapacitor/electric double layercapacitor was considered and its electrochemical properties were characterized by cyclic voltammetryand dc charge/discharge test. The combined capacitor shows excellent capacitor behavior with anoperating voltage up to 1.6 V in KOH aqueous electrolyte. Stable charge/discharge behaviors wereobserved with much higher specific capacitance values of 24 F/g compared with that of EDLC (12 F/g)by introducing 60 percent Ni(0H)_2 in the anode material. By using the modified anode of aNi(OH)_2/carbon nanotubes composite electrode, the specific capacitance of the cell was lesssensitive to discharge current density compared with that of the capacitor employing pure nickelhydroxide as anode. The combined capacitor in this study exhibits high energy density and stablepower characteristics.展开更多
文摘A new sol-gel process for the preparation of ultrafine nickel hydroxideelectrode materials was developed. The composite electrodes consisting of carbon nanotubes andNi(OH)_2 were developed by mixing the hydroxide and carbon nanotubes together in different massratios. In order to enhance energy density, a combined type pseudocapacitor/electric double layercapacitor was considered and its electrochemical properties were characterized by cyclic voltammetryand dc charge/discharge test. The combined capacitor shows excellent capacitor behavior with anoperating voltage up to 1.6 V in KOH aqueous electrolyte. Stable charge/discharge behaviors wereobserved with much higher specific capacitance values of 24 F/g compared with that of EDLC (12 F/g)by introducing 60 percent Ni(0H)_2 in the anode material. By using the modified anode of aNi(OH)_2/carbon nanotubes composite electrode, the specific capacitance of the cell was lesssensitive to discharge current density compared with that of the capacitor employing pure nickelhydroxide as anode. The combined capacitor in this study exhibits high energy density and stablepower characteristics.