Large-scale Mg-8Gd-4Y-1Zn-Mn(wt.%)alloy ingot with a diameter of 315 mm and a length of 2410 mm was prepared through semi-continuous casting.Chemical composition,microstructure and mechanical properties at different l...Large-scale Mg-8Gd-4Y-1Zn-Mn(wt.%)alloy ingot with a diameter of 315 mm and a length of 2410 mm was prepared through semi-continuous casting.Chemical composition,microstructure and mechanical properties at different locations of the samples with as-cast,T4 and T6 heat-treated states,respectively,were investigated.No obvious macro segregation has been detected in the high-quality alloy ingot.The main eutectic structures at all different locations are composed ofα-Mg,Mg3RE-type,Mg5RE-type and LPSO phases.At the edge of ingot,the unusual casting twins including 10-12 extension twins and 10-11 compression twins were observed due to the intensive internal stress.In T4 heat-treated alloy,the micro segregation was eliminated.The remained phases wereα-Mg and LPSO phase.Combined with the remarkable age-hardening response,T6 samples exhibits improved mechanical properties at ambient temperature,which derives from the dense prismaticβ'precipitates and profuse basalγ'precipitates.展开更多
基金financially supported by the National Key Research and Development Program of China(No.2016YFB0301100)the Natural Science Foundation Commission of China(Nos.51571044 and 51874062)+2 种基金the Chongqing foundation and advanced research project(No.cstc2019jcyjzdxmX0010)the Fundamental Research Funds for the Central Universities(Nos.2018CDGFCL0005 and 2019CDXYCL0031)the financial support from the China Scholarship Council(No.201906050113)。
文摘Large-scale Mg-8Gd-4Y-1Zn-Mn(wt.%)alloy ingot with a diameter of 315 mm and a length of 2410 mm was prepared through semi-continuous casting.Chemical composition,microstructure and mechanical properties at different locations of the samples with as-cast,T4 and T6 heat-treated states,respectively,were investigated.No obvious macro segregation has been detected in the high-quality alloy ingot.The main eutectic structures at all different locations are composed ofα-Mg,Mg3RE-type,Mg5RE-type and LPSO phases.At the edge of ingot,the unusual casting twins including 10-12 extension twins and 10-11 compression twins were observed due to the intensive internal stress.In T4 heat-treated alloy,the micro segregation was eliminated.The remained phases wereα-Mg and LPSO phase.Combined with the remarkable age-hardening response,T6 samples exhibits improved mechanical properties at ambient temperature,which derives from the dense prismaticβ'precipitates and profuse basalγ'precipitates.