The Ti_(p)/ZX60 composites with different Ti_(p) contents were prepared by semi-solid stirring casting.After extrusion,the microstructure,work hardening and softening behavior of the Ti_(p)/ZX60 composites were analyz...The Ti_(p)/ZX60 composites with different Ti_(p) contents were prepared by semi-solid stirring casting.After extrusion,the microstructure,work hardening and softening behavior of the Ti_(p)/ZX60 composites were analyzed compared with the ZX60(Mg-6Zn-0.2Ca)alloy.The results showed that the addition of Ti_(p) could not only promote the nucleation of dynamic recrystallized(DRXed)grains,but also be propitious to the refinement of DRXed grains.With increasing Ti_(p) content,the size of DRXed grains decreased accompanied with increasing volume fraction of DRXed grains.As the Ti_(p) content increased to 15 vol.%,the average size and volume fraction of DRXed grains reached to~0.32μm and 93.2%,respectively.Besides,both the strength and elongation were improved by the addition of Ti_(p).With increasing content of Ti_(p),a substantial increase in the strength was achieved with little change in the elongation.However,the elongation decreased sharply when the Ti_(p) content further increased to 15 vol.%.The addition of Ti_(p) led to an increase in the work hardening rate,which gradually increased with increasing Ti_(p) content.However,the softening rate did not demonstrate the same tendency with increasing Ti_(p) content.Unlike the conventional ceramic particles,the Ti_(p) can be deformed in coordination with the matrix alloy,which imparted a higher softening rate to the matrix alloy.Even though the softening rate improved as the Ti_(p) content increased from 5 to 10 vol.%,it dropped deeply as the Ti_(p) content increased to 15 vol.%owing to the fracture of Ti_(p) during extrusion.展开更多
基金supported financially by the National Natural Science Foundation of China (Nos.52271109 and 52001223)the authors also thank the Support from the"the National Key Research and Development Program for Young Scientists" (No.2021YFB3703300)the Special Fund Project for Guiding Local Science and Technology Development by the Central Government (No.YDZJSX2021B019).
文摘The Ti_(p)/ZX60 composites with different Ti_(p) contents were prepared by semi-solid stirring casting.After extrusion,the microstructure,work hardening and softening behavior of the Ti_(p)/ZX60 composites were analyzed compared with the ZX60(Mg-6Zn-0.2Ca)alloy.The results showed that the addition of Ti_(p) could not only promote the nucleation of dynamic recrystallized(DRXed)grains,but also be propitious to the refinement of DRXed grains.With increasing Ti_(p) content,the size of DRXed grains decreased accompanied with increasing volume fraction of DRXed grains.As the Ti_(p) content increased to 15 vol.%,the average size and volume fraction of DRXed grains reached to~0.32μm and 93.2%,respectively.Besides,both the strength and elongation were improved by the addition of Ti_(p).With increasing content of Ti_(p),a substantial increase in the strength was achieved with little change in the elongation.However,the elongation decreased sharply when the Ti_(p) content further increased to 15 vol.%.The addition of Ti_(p) led to an increase in the work hardening rate,which gradually increased with increasing Ti_(p) content.However,the softening rate did not demonstrate the same tendency with increasing Ti_(p) content.Unlike the conventional ceramic particles,the Ti_(p) can be deformed in coordination with the matrix alloy,which imparted a higher softening rate to the matrix alloy.Even though the softening rate improved as the Ti_(p) content increased from 5 to 10 vol.%,it dropped deeply as the Ti_(p) content increased to 15 vol.%owing to the fracture of Ti_(p) during extrusion.