Effects of friction stir spot processing(FSSP)on the microstructures and microhardness of tungsten inert gas(TIG)welded TA15titanium alloy joints were investigated.The macro/micro structural observation and microhardn...Effects of friction stir spot processing(FSSP)on the microstructures and microhardness of tungsten inert gas(TIG)welded TA15titanium alloy joints were investigated.The macro/micro structural observation and microhardness evaluation of the TA15alloy sheets and TA15TIG welded joints were carried out using optical microscope and microhardness tests.The results show that FSSP effectively improves the microstructure and increases the microhardness of the TA15sheets.As for the TIG welded joints,FSSP also effectively improves the microstructure of joints.And the average microhardness value in weld nugget zone is improved significantly,while a small increase of this value in heat affected zone is observed.The hardness in stirring zone is significantly higher than that in the base metal.Two peak values of hardness appear along the width direction in stirring zone.After FSSP,the average hardness of the weld zone of TA15TIG welded joint is significantly higher than that before FSSP.Under the present process parameters,both the surface oxidation in TA15sheets and in TIG welded joints after FSSP are not evident,while the surface forms the bright white layer,which is composed of a great multitude of fine grains.展开更多
基金Project(51405389) supported by the National Natural Science Foundation of ChinaProject(3102015ZY024) supported by the Fundamental Research Funds for the Central Universities,ChinaProject(2014003) supported by the Shanghai Key Laboratory of Digital Manufacture for Thin-walled Structures,China
文摘Effects of friction stir spot processing(FSSP)on the microstructures and microhardness of tungsten inert gas(TIG)welded TA15titanium alloy joints were investigated.The macro/micro structural observation and microhardness evaluation of the TA15alloy sheets and TA15TIG welded joints were carried out using optical microscope and microhardness tests.The results show that FSSP effectively improves the microstructure and increases the microhardness of the TA15sheets.As for the TIG welded joints,FSSP also effectively improves the microstructure of joints.And the average microhardness value in weld nugget zone is improved significantly,while a small increase of this value in heat affected zone is observed.The hardness in stirring zone is significantly higher than that in the base metal.Two peak values of hardness appear along the width direction in stirring zone.After FSSP,the average hardness of the weld zone of TA15TIG welded joint is significantly higher than that before FSSP.Under the present process parameters,both the surface oxidation in TA15sheets and in TIG welded joints after FSSP are not evident,while the surface forms the bright white layer,which is composed of a great multitude of fine grains.