N-doped carbons as one of the most prominent anode materials to replace standard graphite exhibit outstanding Li+storage performance.However,N-doped carbon anodes still suffer from low N-doping levels and low initial ...N-doped carbons as one of the most prominent anode materials to replace standard graphite exhibit outstanding Li+storage performance.However,N-doped carbon anodes still suffer from low N-doping levels and low initial Coulombic efficiency(ICE).In this study,high N-doped and low graphitic-N carbons(LGNCs)with enhanced ICE were synthesized by taking advantage of a denitrification strategy for graphitic carbon nitride(g-C_(3)N_(4)).In brief,more than 14.5 at%of N from g-C_(3)N_(4)(55.1 at%N)was retained by reacting graphitic-N with lithium,which was subsequently removed.As graphitic-N is largely responsible for the irreversible capacity,the anode's performance was significantly increased.Compared to general N-doped carbons with high graphitic-N proportion(>50%)and low N content(<15 at%),LGNCs delivered a low proportion of 10.8%-17.2% within the high N-doping content of 14.5-42.7 at%,leading to an enhanced specific capacity of 1499.9mAh g^(-1) at an ICE of 93.7% for the optimal sample of LGNC(4:1).This study provides a facile strategy to control the N content and speciation,achieving both high Li+storage capacity and high ICE,and thus promoting research and application of N-doped carbon materials.展开更多
基金National Natural Science Foundation of China,Grant/Award Number:51777138Deutsche Forschungsgemeinschaft(DFG,German Research Foundation),Grant/Award Number:491183248Open Access Publishing Fund of the University of Bayreuth。
文摘N-doped carbons as one of the most prominent anode materials to replace standard graphite exhibit outstanding Li+storage performance.However,N-doped carbon anodes still suffer from low N-doping levels and low initial Coulombic efficiency(ICE).In this study,high N-doped and low graphitic-N carbons(LGNCs)with enhanced ICE were synthesized by taking advantage of a denitrification strategy for graphitic carbon nitride(g-C_(3)N_(4)).In brief,more than 14.5 at%of N from g-C_(3)N_(4)(55.1 at%N)was retained by reacting graphitic-N with lithium,which was subsequently removed.As graphitic-N is largely responsible for the irreversible capacity,the anode's performance was significantly increased.Compared to general N-doped carbons with high graphitic-N proportion(>50%)and low N content(<15 at%),LGNCs delivered a low proportion of 10.8%-17.2% within the high N-doping content of 14.5-42.7 at%,leading to an enhanced specific capacity of 1499.9mAh g^(-1) at an ICE of 93.7% for the optimal sample of LGNC(4:1).This study provides a facile strategy to control the N content and speciation,achieving both high Li+storage capacity and high ICE,and thus promoting research and application of N-doped carbon materials.