Iron nugget and boron-rich slag can be obtained in a short time through high-temperature reduction of boron- bearing iron concentrate by carbonaceous material, both of which are agglomerated together as a carbon compo...Iron nugget and boron-rich slag can be obtained in a short time through high-temperature reduction of boron- bearing iron concentrate by carbonaceous material, both of which are agglomerated together as a carbon composite pellet. This is a novel flow sheet for the comprehensive utilization of boron-bearing iron concentrate to produce a new kind of man-made boron ore. The effect of reducing agent species （i.e., carbon species） on the reduction and melting process of the composite pellet was investigated at a laboratory scale in the present work. The results show that, the reduction rate of the composite pellet increases from bituminite, anthracite, to coke at temperatures ranging from 950 to 1300~C. Reduction temperature has an important effect on the microstructure of reduced pellets. Carbon species also affects the behavior of reduced metallic iron particles. The anthracite-bearing composite pellet melts faster than the bituminite- bearing composite pellet, and the coke-bearing composite pellet cannot melt due to the high fusion point of coke ash. With anthracite as the reducing agent, the recovery rates of iron and boron are 96.5% and 95.7%, respectively. This work can help us get a further understanding of the new process mechanism.展开更多
Basic physicochemical properties of the dust from Laiwu Iron and Steel Co. Ltd. were studied. It is found that C, Zn, K, Na, etc. exist in the fabric filter dust, off gas （OG） sludge, fine ash in converter, and elec...Basic physicochemical properties of the dust from Laiwu Iron and Steel Co. Ltd. were studied. It is found that C, Zn, K, Na, etc. exist in the fabric filter dust, off gas （OG） sludge, fine ash in converter, and electrical field dust in sinter. Among these, OG sludge gives the finest particle, more than 90% of which is less than 2.51 mm. The dust can lead to a serious negative influence on the production of sintering and blast furnaces （BF） if it is recycled in sintering. The briquette and reduction experimental results showed that the qualified strength could be obtained in the case of 8wt% molasses or 4wt% QT-10 added as binders. Also, more than 75% of metallization ratio, more than 95% of dezincing ratio, as well as more than 80% of K and Na removal rates were achieved for the briquettes kept at 1250℃ for 15 min during the direct reduction process. SEM observation indicated that the rates of indirect reduction and carbonization became dominating when the bri-quettes were kept at 1250℃ for 6 min.展开更多
基金support by the National Natural Science Foundation of China(No.51274033)
文摘Iron nugget and boron-rich slag can be obtained in a short time through high-temperature reduction of boron- bearing iron concentrate by carbonaceous material, both of which are agglomerated together as a carbon composite pellet. This is a novel flow sheet for the comprehensive utilization of boron-bearing iron concentrate to produce a new kind of man-made boron ore. The effect of reducing agent species （i.e., carbon species） on the reduction and melting process of the composite pellet was investigated at a laboratory scale in the present work. The results show that, the reduction rate of the composite pellet increases from bituminite, anthracite, to coke at temperatures ranging from 950 to 1300~C. Reduction temperature has an important effect on the microstructure of reduced pellets. Carbon species also affects the behavior of reduced metallic iron particles. The anthracite-bearing composite pellet melts faster than the bituminite- bearing composite pellet, and the coke-bearing composite pellet cannot melt due to the high fusion point of coke ash. With anthracite as the reducing agent, the recovery rates of iron and boron are 96.5% and 95.7%, respectively. This work can help us get a further understanding of the new process mechanism.
文摘Basic physicochemical properties of the dust from Laiwu Iron and Steel Co. Ltd. were studied. It is found that C, Zn, K, Na, etc. exist in the fabric filter dust, off gas （OG） sludge, fine ash in converter, and electrical field dust in sinter. Among these, OG sludge gives the finest particle, more than 90% of which is less than 2.51 mm. The dust can lead to a serious negative influence on the production of sintering and blast furnaces （BF） if it is recycled in sintering. The briquette and reduction experimental results showed that the qualified strength could be obtained in the case of 8wt% molasses or 4wt% QT-10 added as binders. Also, more than 75% of metallization ratio, more than 95% of dezincing ratio, as well as more than 80% of K and Na removal rates were achieved for the briquettes kept at 1250℃ for 15 min during the direct reduction process. SEM observation indicated that the rates of indirect reduction and carbonization became dominating when the bri-quettes were kept at 1250℃ for 6 min.