To design a promising Al−Si filler alloy with a relatively low melting-point,good strength and plasticity for the Cu/Al joint,the Cu,Ni,Zr and Er elements were innovatively added to modify the traditional Al−Si eutect...To design a promising Al−Si filler alloy with a relatively low melting-point,good strength and plasticity for the Cu/Al joint,the Cu,Ni,Zr and Er elements were innovatively added to modify the traditional Al−Si eutectic filler.The microstructure and mechanical properties of filler alloys and Cu/Al joints were investigated.The result indicated that the Al−Si−Ni−Cu filler alloys mainly consisted of Al(s,s),Al_(2)(Cu,Ni)and Si(s,s).The Al−10Si−2Ni−6Cu filler alloy exhibited relatively low solidus(521℃)and liquidus(577℃)temperature,good tensile strength(305.8 MPa)and fracture elongation(8.5%).The corresponding Cu/Al joint brazed using Al−10Si−2Ni−6Cu filler was mainly composed of Al_(8)(Mn,Fe)_(2)Si,Al_(2)(Cu,Ni)3,Al(Cu,Ni),Al_(2)(Cu,Ni)and Al(s,s),yielding a shear strength of(90.3±10.7)MPa.The joint strength was further improved to(94.6±2.5)MPa when the joint was brazed using the Al−10Si−2Ni−6Cu−0.2Er−0.2Zr filler alloy.Consequently,the(Cu,Ni,Zr,Er)-modified Al−Si filler alloy was suitable for obtaining high-quality Cu/Al brazed joints.展开更多
基金the financial support from the Primary Research&Development Plan of Zhejiang Province,China(No.2021C01178)the National MCF Energy R&D Program,China(No.2019YFE03100400)+1 种基金the National Natural Science Foundation of China(Nos.51705457,51975530,52005445,52175368)the Natural Science Foundation of Zhejiang Province,China(Nos.LQ21E050015,LQ21E050018).
文摘To design a promising Al−Si filler alloy with a relatively low melting-point,good strength and plasticity for the Cu/Al joint,the Cu,Ni,Zr and Er elements were innovatively added to modify the traditional Al−Si eutectic filler.The microstructure and mechanical properties of filler alloys and Cu/Al joints were investigated.The result indicated that the Al−Si−Ni−Cu filler alloys mainly consisted of Al(s,s),Al_(2)(Cu,Ni)and Si(s,s).The Al−10Si−2Ni−6Cu filler alloy exhibited relatively low solidus(521℃)and liquidus(577℃)temperature,good tensile strength(305.8 MPa)and fracture elongation(8.5%).The corresponding Cu/Al joint brazed using Al−10Si−2Ni−6Cu filler was mainly composed of Al_(8)(Mn,Fe)_(2)Si,Al_(2)(Cu,Ni)3,Al(Cu,Ni),Al_(2)(Cu,Ni)and Al(s,s),yielding a shear strength of(90.3±10.7)MPa.The joint strength was further improved to(94.6±2.5)MPa when the joint was brazed using the Al−10Si−2Ni−6Cu−0.2Er−0.2Zr filler alloy.Consequently,the(Cu,Ni,Zr,Er)-modified Al−Si filler alloy was suitable for obtaining high-quality Cu/Al brazed joints.