In this study,nitrogen doped electrochemically exfoliated reduced graphene oxide and carbon black supported platinum(Pt/Nr EGO_(2)-CB_(3))has been prepared to enhance the performance and durability of hightemperature ...In this study,nitrogen doped electrochemically exfoliated reduced graphene oxide and carbon black supported platinum(Pt/Nr EGO_(2)-CB_(3))has been prepared to enhance the performance and durability of hightemperature PEMFCs with lower Pt loading.On the one hand,Pt/Nr EGO_(2)-CB_(3)with the strong interaction between the Pt and nitrogen(N)prevent agglomeration of Pt particles and Pt particles is 5.46±1.46 nm,which is smaller than that of 6.78±1.34 nm in Pt/C.Meanwhile,ECSA of Pt/Nr EGO_(2)-CB_(3)decrease 13.65%after AST,which is much lower than that of 97.99%in Pt/C.On the other hand,the Nr EGO flakes in MEAac act as a barrier to mitigate phosphoric acid redistribution,which improves the formation of triple-phase boundaries(TPBs)and gives stable operation of the MEAacwith a lower decay rate of 0.02 mV h^(-1)within100 h.After steady-state operation,the maximum power density of Pt/Nr EGO_(2)-CB_(3)(0.411 W cm^(-2))is three times higher than that of conventional Pt/C(0.134 W cm^(-2))in high-temperature PEMFCs.After AST,the mass transfer resistance of Pt/Nr EGO_(2)-CB_(3)electrode(0.560Ωcm^(2))is lower than that in Pt/C(0.728Ωcm^(2)).展开更多
基金supported by the Engineering and Physical Sciences Research Council(EPSRC)(EP/P009050/1 and EP/S021531/1)Tthe Henry Royce Institute for Advanced Materials,funded through the EPSRC grants(EP/R00661X/1,EP/S019367/1,EP/P025021/1 and EP/P025498/1)。
文摘In this study,nitrogen doped electrochemically exfoliated reduced graphene oxide and carbon black supported platinum(Pt/Nr EGO_(2)-CB_(3))has been prepared to enhance the performance and durability of hightemperature PEMFCs with lower Pt loading.On the one hand,Pt/Nr EGO_(2)-CB_(3)with the strong interaction between the Pt and nitrogen(N)prevent agglomeration of Pt particles and Pt particles is 5.46±1.46 nm,which is smaller than that of 6.78±1.34 nm in Pt/C.Meanwhile,ECSA of Pt/Nr EGO_(2)-CB_(3)decrease 13.65%after AST,which is much lower than that of 97.99%in Pt/C.On the other hand,the Nr EGO flakes in MEAac act as a barrier to mitigate phosphoric acid redistribution,which improves the formation of triple-phase boundaries(TPBs)and gives stable operation of the MEAacwith a lower decay rate of 0.02 mV h^(-1)within100 h.After steady-state operation,the maximum power density of Pt/Nr EGO_(2)-CB_(3)(0.411 W cm^(-2))is three times higher than that of conventional Pt/C(0.134 W cm^(-2))in high-temperature PEMFCs.After AST,the mass transfer resistance of Pt/Nr EGO_(2)-CB_(3)electrode(0.560Ωcm^(2))is lower than that in Pt/C(0.728Ωcm^(2)).