黄钾铁矾对硫脲浸金的影响及草酸盐的作用机理

研究生物氧化产生的黄钾铁矾对酸性硫脲浸金的影响,并探讨草酸添加剂的作用机制。结果表明,黄钾铁矾会增加硫脲的消耗和阻碍金的溶解。黄钾铁矾能显著提高硫脲的分解,阻碍金的溶解。黄钾铁矾造成不利影响的主要原因可能是酸性溶液中黄钾铁矾释放的铁离子使溶液浆电位增加,从而加速硫脲的分解,并加剧硫脲分解产生的钝化物种对金表面的钝化作用。添加草酸盐可以有效削弱黄钾铁矾的不利影响,表现为明显降低硫脲的消耗和促进金的溶解。通过溶液电位、Zeta电位和XPS分析,揭示草酸的可能作用机理。草酸盐不仅可以通过与Fe^(3+)配位减弱Fe^(3+)与硫脲之间的相互作用,还可以通过无差别吸附和静电斥力阻止钝化产物在金表面包裹。

采用钠化焙烧-还原浸出联合工艺从废Pd/Al_(2)O_(3)催化剂中经济高效回收Pd和Al_(2)O_(3)

开发了钠焙烧-还原浸出联合工艺从废Pd/Al_(2)O_(3)催化剂中回收Pd和Al_(2)O_(3)。钠化焙烧热力学分析表明,在最佳的Na_(2)O/Al_(2)O_(3)摩尔比和温度下,NaOH、Na_(2)CO_(3)和Na_(2)C2O4均可以与Al_(2)O_(3)完全反应生成Na Al O2。NaOH、Na_(2)CO_(3)和Na_(2)C_(2)O_(4)的焙烧渣经水浸后,Al_(2)O_(3)浸出率分别为99.6%、61.0%和55.3%。机械活化-NaOH无水焙烧工艺避免了焙烧渣的固结且可获得较高的Al_(2)O_(3)浸出率。N_(2)H_(4)·H_(2)O还原浸出避免了水浸过程中Pd的溶解损失且催化剂中99.7%的Al_(2)O_(3)被浸出。最终得到Na Al O2浸出液和富钯渣,其中有价的铝和钯可被进一步回收。

Individual with concurrent chest wall tuberculosis and triplenegative essential thrombocythemia:A case report

BACKGROUND Chest wall tuberculosis(TB)and triple-negative essential thrombocythemia(TNET)are rare medical conditions,and their combination is extremely rare globally.Only one case of TB peritonitis with thrombocytosis has been reported,which was identified in 1974.CASE SUMMARY Herein,we report the case of a 23-year-old man with concurrent chest wall mass and TN-ET.The patient presented to a local hospital due to having a headache and low-grade fever for 2 d,with their bodily temperature fluctuating at around 36.8°C.Hematological analysis showed a high platelet count of 1503×109/L.Subsequently,the patient visited our hospital for further investigation.Computed tomography of the chest suggested a submural soft tissue density shadow in the left lower chest wall.After surgical resection,the pathological findings of the swelling were reported as TB with massive caseous necrosis.According to the World Health Organization diagnostic criteria,the patient was diagnosed with TN-ET,as they met the requirement of four main criteria or the first three main criteria and one secondary criterion.The patient was eventually diagnosed with chest wall TB with TN-ET,which is extremely rare.CONCLUSION Chest wall TB is rare.TN-ET diagnosis requires secondary factor exclusion and satisfaction of primary diagnostic criteria.miRNA,combined with the methylation process,could explain suppressor of cytokine signaling(SOCS)1 and SOCS3 downregulation in ET-JAK2V617F-negative patients.The miRNA could participate in JAK2 pathway activation.SOCS3 may be a novel MPN biomarker.

Extraction of manganese and zinc from their compound ore by reductive acid leaching

Comprehensive utilization of low grade manganese?zinc compound ore containing lead and silver with a method of reductive acid leaching was studied.According to theφ?pH diagram of Mn?Zn?H2O system,Mn and Zn can be leached simultaneously in the pH range of?2to5.61.The results showed that both hydrogen peroxide and sucrose were effective reductants which could intensify the simultaneous leaching of Mn and Zn into leachate as well as enrich Pb and Ag in the residue.95.88%of Mn and99.23%of Zn were extracted when the compound ore was leached with hydrogen peroxide in sulfuric acid media,meanwhile the contents of Pb and Ag in the residue were enriched to13.21%and489.36g/t,respectively.When sucrose was used as the reductant,the leaching efficiencies of Mn and Zn separately achieved98.26%and99.62%,and contents of Pb and Ag in the residue were as high as13.92%and517.87g/t,respectively.

Consolidation mechanism of gold concentrates containing sulfur and carbon during oxygen-enriched air roasting

Consolidation in calcines is a common problem in the oxygen-enriched air roasting of refractory gold concentrates containing sulfur and carbon when the initial temperature is greater than 600°C. To determine the phases that caused consolidation, gold concentrates were roasted under different conditions and the calcines were mainly detected by X-ray diffraction (XRD). The possible underlying mechanism was then studied through comparisons of the XRD patterns of different calcines. The results indicated that the generation of calcium magnesium silicate, iron-doped calcium aluminosilicate, and calcium aluminate caused the consolidation. Furthermore, an enriched oxygen atmosphere accelerated the oxidation reaction and the emitted heat increased the local temperature in calcines. The local temperature was inferred to have increased to the generation temperature zone of the corresponding liquid phases. Oxidation of the pyrite and decomposition of the dolomite and muscovite mainly occurred at the initial stage of oxygen-enriched air roasting. Calcium was confirmed to be essential to the consolidation process. © 2017, University of Science and Technology Beijing and Springer-Verlag Berlin Heidelberg.