Effects of co-precipitation temperature on structure and properties of La and Y doped cerium zirconium mixed oxides

Due to the oxygen storage and release properties,cerium zirconium mixed oxides are recognized as the key material in automotive three-way catalysts.To reveal the effects of co-precipitation temperature on structure,physical and chemical properties of multi-doped cerium zirconium mixed oxides,a series of La and Y doped cerium zirconium mixed oxides(CZLYs)were synthesized via a co-precipitation method,and the physical and chemical properties of CZLYs were systemically characterized by XRD,N_(2) adsorption−desorption,TEM,XPS,oxygen storage capacity(OSC)and hydrogen temperature programmed reduction(H_(2)-TPR).The results show that co-precipitation temperature is an important parameter to influence the crystal size,oxygen storage capacity and thermal stability of CZLYs.When the co-precipitation temperature was 60℃,the best redox properties and thermal stability of CZLYs were obtained.After thermal treatment at 1100℃for 10 h,the specific surface area and oxygen storage capacity of the corresponding aged sample were 15.42 m^(2)/g and 497.7μmol/g,respectively.In addition,a mechanism was proposed to reveal the effects of co-precipitation temperature on the structure and properties of CZLYs.

A novel Ce_(0.485)Zr_(0.485)Y_(0.03)O_(2) composite oxide with surface doping of Y and its application in Pd-only three-way catalyst

The ceria-zirconia compound oxide-supported noble metal Pd(Pd@CZ)is widely used in three-way catalyst.Moreover,the surface structure of CZ plays an important role in catalytic activity of Pd.However,how to regulate the surface structure of CZ and clarify the structure–activity relationship is still a challenge.In this paper,a strategy is proposed to develop high activity Pd@CZ nanocatalysts by tuning Y doping sites in CZ.The precipitate-deposition method is developed to prepare the novel Ce_(0.485)Zr_(0.485)Y_(0.03)O_(2) composite with surface doping of Y(CZ-Y-S).In addition,the Pd@CZ-Y-S(Pd supported on CZ-Y-S)exhibits superior catalytic activity for HC,CO,and NO oxide,wherein,for CO and C_(3)H_(6) oxidation,the low-temperature activity of Pd@CZ-Y-S is still 20%higher than that of Pd@CZ-Y-B(Y bulk doping)and commercial Pd@CZ after 1000℃/4 h aging.The effect mechanism is further studied by density functional theory(DFT)calculation.Compared with Pd@CZ-Y-B,Pd@CZ-Y-S shows the lower CO oxide reaction energy barriers due to the weaker adsorption strength of O2.The Y surface doping strategy could provide valuable insights for the development of highly efficient Pd@CZ catalyst with extensive applications.