Cerium-based sealing treatment was developed for Mg-Al hydrotalcite film on AZ91D Mg alloy,and the influence of cerium salt solution was investigated to modify the surface integrity and corrosion resistance.Scanning e...Cerium-based sealing treatment was developed for Mg-Al hydrotalcite film on AZ91D Mg alloy,and the influence of cerium salt solution was investigated to modify the surface integrity and corrosion resistance.Scanning electron microscope(SEM)and X-ray diffraction(XRD)measurements were carried out to analyze the surface morphology and phase composition.The corrosion resistance of Mg-Al hydrotalcite film after sealing treatment was evaluated by the polarization curve and electrochemical impedance spectroscopy(EIS)tests.The results showed that lower concentration of Ce-containing solution was beneficial to seal the micro-cracks on Mg-Al hydrotalcite film,and improve the surface integrity and corrosion resistance;higher concentration of Ce-containing solution could seal fewer micro-cracks,and the corrosion resistance was decreased owing to the disintegration of Mg-Al hydrotalcite film.展开更多
基金supported by the National Natural Science Foundation of China(No.51701093)the Natural Science Foundation of Jiangsu Province(No.BK20170764)+2 种基金the Six Talent Peaks(No.2015-XCL-025)the Qing Lan Project of Jiangsu Province,the Practice Innovation Program for graduate students of Jiangsu Province(No.SJZZ16_0292)the Research Fund of Nanjing Institute of Technology(No.JCYJ201603).
文摘Cerium-based sealing treatment was developed for Mg-Al hydrotalcite film on AZ91D Mg alloy,and the influence of cerium salt solution was investigated to modify the surface integrity and corrosion resistance.Scanning electron microscope(SEM)and X-ray diffraction(XRD)measurements were carried out to analyze the surface morphology and phase composition.The corrosion resistance of Mg-Al hydrotalcite film after sealing treatment was evaluated by the polarization curve and electrochemical impedance spectroscopy(EIS)tests.The results showed that lower concentration of Ce-containing solution was beneficial to seal the micro-cracks on Mg-Al hydrotalcite film,and improve the surface integrity and corrosion resistance;higher concentration of Ce-containing solution could seal fewer micro-cracks,and the corrosion resistance was decreased owing to the disintegration of Mg-Al hydrotalcite film.