The cavitation erosion of weld joint and base metal of China low activation martensitic（CLAM）steel in liquid lead-bismuth eutectic alloy（LBE）at 550°C was investigated to simulate the cavitation erosion of the...The cavitation erosion of weld joint and base metal of China low activation martensitic（CLAM）steel in liquid lead-bismuth eutectic alloy（LBE）at 550°C was investigated to simulate the cavitation erosion of the first wall and the nuclear main pump impeller in the accelerator driven sub-critical system（ADS）.A suit of ultrasonic cavitation facility was self-designed to study the cavitation erosion.By studying the surface micro topography,roughness and mean pit depth of the tested specimens,it was found that some crater clusters and large scale cracks appeared on the tested specimen surface after the formation of numerous single craters,and the base metal exhibited much better cavitation erosion resistance than the weld bead due to the difference in their mechanical properties and microstructures.In addition,by comparing the results of static corrosion and cavitation erosion,it could be concluded that the cavitation erosion and the dissolution and oxidation corrosion in liquid LBE would accelerate mutually.展开更多
基金supported by the National Natural Science Foundation of China with Grant Nos.51375216 and 51505197the Open-Fund Research of State Key Lab of Advanced Welding and Joining with Grant No.AWJ-16-M07the Fusion Digital Simulation(FDS)Team for support the CLAM steel
文摘The cavitation erosion of weld joint and base metal of China low activation martensitic（CLAM）steel in liquid lead-bismuth eutectic alloy（LBE）at 550°C was investigated to simulate the cavitation erosion of the first wall and the nuclear main pump impeller in the accelerator driven sub-critical system（ADS）.A suit of ultrasonic cavitation facility was self-designed to study the cavitation erosion.By studying the surface micro topography,roughness and mean pit depth of the tested specimens,it was found that some crater clusters and large scale cracks appeared on the tested specimen surface after the formation of numerous single craters,and the base metal exhibited much better cavitation erosion resistance than the weld bead due to the difference in their mechanical properties and microstructures.In addition,by comparing the results of static corrosion and cavitation erosion,it could be concluded that the cavitation erosion and the dissolution and oxidation corrosion in liquid LBE would accelerate mutually.