Tailings from the vanadium extraction process are discarded each year as waste,which contain approximately 30 wt%of Fe.In our previous work,we extracted Fe and Mn from vanadium slag,and Fe and Mn existed in the form o...Tailings from the vanadium extraction process are discarded each year as waste,which contain approximately 30 wt%of Fe.In our previous work,we extracted Fe and Mn from vanadium slag,and Fe and Mn existed in the form of FeCl_(2) and MnCl_(2) after chlorination by NH_(4) Cl to achieve effective and green usage of waste containing Fe and Mn.In this work,square wave voltammetry(SWV)and cyclic voltammetry(CV)were applied to investigate the electrochemical behaviors of Fe^(2+)and Mn^(2+)in Na Cl-KCl melt at 800℃.The reduction processes of Fe^(2+)and Mn^(2+)were found to involve one step.The diffusion coefficients of FeCl_(2) and Mn Cl_(2) in molten salt of eutectic mixtures Na Cl-KCl molten salt were measured.The electrodeposition of Fe and Mn were performed using two electrodes at a constant cell voltage.The Mn/Fe mass ratio of the electrodeposited product in Na Cl-KCl-2.13 wt%FeCl_(2)-1.07 wt%Mn Cl_(2) was 0.0625 at 2.3 V.After the electrolysis of NaCl-KCl-2.13 wt%Fe Cl_(2)-1.07 wt%MnCl_(2) melted at 2.3 V,the electrolysis was again started under 3.0 V and the Mn/Fe mass ratio of the electrodeposited product was 36.4.This process provides a novel method to effectively separate Fe and Mn from simulated chlorinated vanadium slag.展开更多
During the smelting process of the high Al steels,the reaction between SiOin molten slag and dissolved aluminum in liquid steel always takes place.This aluminathermic reduction reaction will lead to the substitution o...During the smelting process of the high Al steels,the reaction between SiOin molten slag and dissolved aluminum in liquid steel always takes place.This aluminathermic reduction reaction will lead to the substitution of 1mol SiOfor 2/3mol AlO.Therefore,the investigations about the influence of the ratio of AlOto SiOon viscosity and structure changes of mould flux during this process are very necessary.The viscosity variation of CaO-SiO-AlO-CaFv2 melts was studied by changing compositions considering the aluminathermic reduction reaction.It was found that viscosity increased monotonously with gradually increasing the substitution extent.According to the Raman analysis,the substitution of AlOfor SiOleads to the decrease of non-bridging oxygen but the increase of bridging oxygen.Therefore,degree of polymerization and viscosity increase as the substitution extent increases.By comparing the measured viscosities with the model calculated values,it was found that both the recently developed Zhang′s model and Roboud model could describe the viscosity variation behavior of CaO-SiO-AlO-CaFmelts very well.展开更多
基金the National Natural Science Foundation of China(Nos.51904286,51922003,51774027 and 51734002)the China Postdoctoral Science Foundation(No.2019M650848)。
文摘Tailings from the vanadium extraction process are discarded each year as waste,which contain approximately 30 wt%of Fe.In our previous work,we extracted Fe and Mn from vanadium slag,and Fe and Mn existed in the form of FeCl_(2) and MnCl_(2) after chlorination by NH_(4) Cl to achieve effective and green usage of waste containing Fe and Mn.In this work,square wave voltammetry(SWV)and cyclic voltammetry(CV)were applied to investigate the electrochemical behaviors of Fe^(2+)and Mn^(2+)in Na Cl-KCl melt at 800℃.The reduction processes of Fe^(2+)and Mn^(2+)were found to involve one step.The diffusion coefficients of FeCl_(2) and Mn Cl_(2) in molten salt of eutectic mixtures Na Cl-KCl molten salt were measured.The electrodeposition of Fe and Mn were performed using two electrodes at a constant cell voltage.The Mn/Fe mass ratio of the electrodeposited product in Na Cl-KCl-2.13 wt%FeCl_(2)-1.07 wt%Mn Cl_(2) was 0.0625 at 2.3 V.After the electrolysis of NaCl-KCl-2.13 wt%Fe Cl_(2)-1.07 wt%MnCl_(2) melted at 2.3 V,the electrolysis was again started under 3.0 V and the Mn/Fe mass ratio of the electrodeposited product was 36.4.This process provides a novel method to effectively separate Fe and Mn from simulated chlorinated vanadium slag.
基金Item Sponsored by National Natural Science Foundation of China(51304018,51174022,51474141)
文摘During the smelting process of the high Al steels,the reaction between SiOin molten slag and dissolved aluminum in liquid steel always takes place.This aluminathermic reduction reaction will lead to the substitution of 1mol SiOfor 2/3mol AlO.Therefore,the investigations about the influence of the ratio of AlOto SiOon viscosity and structure changes of mould flux during this process are very necessary.The viscosity variation of CaO-SiO-AlO-CaFv2 melts was studied by changing compositions considering the aluminathermic reduction reaction.It was found that viscosity increased monotonously with gradually increasing the substitution extent.According to the Raman analysis,the substitution of AlOfor SiOleads to the decrease of non-bridging oxygen but the increase of bridging oxygen.Therefore,degree of polymerization and viscosity increase as the substitution extent increases.By comparing the measured viscosities with the model calculated values,it was found that both the recently developed Zhang′s model and Roboud model could describe the viscosity variation behavior of CaO-SiO-AlO-CaFmelts very well.