CrAlYN coatings with different Y contents(0,5 and 12 at.%)were deposited by cathodic arc evaporation to investigate the influence of Y-addition on the structure,mechanical and thermal properties of CrAlN coatings by u...CrAlYN coatings with different Y contents(0,5 and 12 at.%)were deposited by cathodic arc evaporation to investigate the influence of Y-addition on the structure,mechanical and thermal properties of CrAlN coatings by using X-ray diffraction,scanning electron microscopy,differential scanning calorimetry,thermal gravimetric analysis and nanoindentation.The structural transformation of single phase cubic Cr_(0.42)Al_(0.58)N and Cr_(0.39)Al_(0.56)Y_(0.05)N coatings to cubic−wurtzite mixed Cr_(0.32)Al_(0.56)Y_(0.12)N coating leads to a drop in hardness from(30.2±0.7)GPa of Cr_(0.42)Al_(0.58)N and(32.0±1.0)GPa of Cr_(0.39)Al_(0.56)Y_(0.05)N to(25.2±0.7)GPa of Cr_(0.32)Al_(0.56)Y_(0.12)N.The incorporation of 5 at.%Y retards the thermal decomposition of CrAlN,verified by the postponed precipitation of w-AlN and N-loss upon annealing.Correspondingly,Cr_(0.39)Al_(0.56)Y_(0.05)N coating consistently exhibits the highest hardness value during thermal annealing.Nevertheless,alloying with Y exerts an adverse effect on the oxidation resistance of CrAlN.展开更多
基金The authors are grateful for the financial supports from the National Natural Science Foundation of China(No.51775560).
文摘CrAlYN coatings with different Y contents(0,5 and 12 at.%)were deposited by cathodic arc evaporation to investigate the influence of Y-addition on the structure,mechanical and thermal properties of CrAlN coatings by using X-ray diffraction,scanning electron microscopy,differential scanning calorimetry,thermal gravimetric analysis and nanoindentation.The structural transformation of single phase cubic Cr_(0.42)Al_(0.58)N and Cr_(0.39)Al_(0.56)Y_(0.05)N coatings to cubic−wurtzite mixed Cr_(0.32)Al_(0.56)Y_(0.12)N coating leads to a drop in hardness from(30.2±0.7)GPa of Cr_(0.42)Al_(0.58)N and(32.0±1.0)GPa of Cr_(0.39)Al_(0.56)Y_(0.05)N to(25.2±0.7)GPa of Cr_(0.32)Al_(0.56)Y_(0.12)N.The incorporation of 5 at.%Y retards the thermal decomposition of CrAlN,verified by the postponed precipitation of w-AlN and N-loss upon annealing.Correspondingly,Cr_(0.39)Al_(0.56)Y_(0.05)N coating consistently exhibits the highest hardness value during thermal annealing.Nevertheless,alloying with Y exerts an adverse effect on the oxidation resistance of CrAlN.