A method to study interface diffusion of arsenic into a Nb-Ti microalloyed low carbon steel

A novel diffusion couple method was used to investigate the interface diffusion of arsenic into a Nb-Ti microalloyed low carbon steel and its effects on phase transformation at the interface. It is discovered that the content of arsenic has great effect on grain growth and phase transformation at high temperature. When the arsenic content is no more than lwt%, there is no obvious grain growth and no obvious ferrite transitional region formed at the diffusion interface. However, when the arsenic content is no less than 5wt%, the grain grows very rapidly. In addition, the arsenic-enriched ferrite transitional layer forms at the diffusion interface in the hot-rolling process, which results from a slower diffusion rate of arsenic atoms than that of carbon in ferrite.

Evolution of carbides and carbon content in matrix of an ultra-high carbon sintered steel during heat treatment process

DTA, thermal expansion, XRD, and SEM were used to evaluate the effect of quenching temperature on the mechanical properties and microstructure of a novel sintered steel Fe-6Co-1Ni-5Cr-5Mo-1C. Lattice parameters and the mass fraction of carbon dissolved in the matrix of the steel quenched were investigated. It is discovered that the hardness of the steel increases with quenching temperature in the range of 840-900℃ and remains constant in the range of 900 to 1100℃. It decreases rapidly when the temperature is higher than 1100℃. The mass fraction of carbon dissolved in the matrix of the steel quenched at 840℃ is 0.38, but when the quenching temperature is increased to 1150℃, it increases to 0.98. The carbides formed during sintering are still present at grain boundaries and in the matrix of the steel quenched at low quenching temperatures, such as 840℃. When the quenching temperature is increased to 1150℃, most of the carbides at grain boundaries are dissolved with just a small amount of spherical M23C6 existing in the matrix of the quenched steel.

Grain boundary segregation of minor arsenic and nitrogen at elevated temperatures in a microalloyed steel

Auger electron spectroscopy （AES） was used to investigate the grain boundary segregation of arsenic and nitrogen in a kind of microalloyed steel produced by a compact strip production （CSP） technology at 950 to 1100℃, which are similar to the hot working temperature of the steel on a CSP production line. It was discovered that arsenic segregated on grain boundaries when the steel was annealed at 950℃ for 2 h. When the annealing temperature increased to 1100℃, arsenic was also found to have segregated on grain boundaries in the early annealing stage, for instance, within the first 5 min annealing time. However, if the holding time of the steel at this temperature increased to 2 h, arsenic diffused away from grain boundaries into the matrix again. Nitrogen was not found to have segregated on grain boundaries when the steel was annealed at a relatively low temperature, such as 950℃. But when the annealing temperature increased to 1100℃, nitrogen was detected to have segregated at grain boundaries in the steel.

Effects of the microstructure of twin roll cast and hot rolled plates on the surface quality of presensitized plates

The effect of the microstructure of plates fabricated both in the traditional process, involving casting, hot rolling and cold rolling （HR）, and in the novel twin roll casting ＋ cold rolling （TRC） process on the surface quality of presensitized （PS） plates was analyzed by optical microscopy （OM）, scanning electron microscopy （SEM）, and energy-dispersive X-ray spectroscopy （EDXS）. The formation of pores on the surface of the electrolyzed HR plate could be attributed to the presence of approximately 1-μm-sized large Al-Fe precipitates in the HR plate compared to the smaller precipitates in the TRC plate. Moreover, residual graphite lubricants used during the TRC process were entrapped on the surface of the TRC plate during the subsequent rolling process. The entrapped pollutants tended to further deteriorate the formation of pores on the surface of the TRC plate, and no residual carbon was detected on the surface of the HR plate. Furthermore, the surface quality of the TRC plate can be improved by surface cleaning before the cold rolling process, which could dramatically lower the residual graphite on the surface.

Heteroatom-Doped Black Phosphorus and Its Application:A Review

Few-layer black phosphorus(BP)is a promising semiconductor with excellent optoelectronic properties.However,the poor stabilization and strong asymmetry between electron and hole transports hinder the application of BP.Doping of heteroatoms is an effective strategy to regulate the electronic structure and stability of BP without sacrificing its unique 2D structure,which is a promising way to tune the physico-chemical properties of BP for various applications.In this review,the recent advances in doping engineer-ing of BP are summarized,involving the theoretical prediction of new characteristic for doped BP and the corresponding experimental synthesis methods.The effects of dopant atoms on the structure and perfor-mance of BP and its related applications,such as the field-effect transistors,optoelectronic devices,in-verter devices,and catalysis,are also summarized.