A one-step overall strategy from surface to bulk was proposed to simultaneously synthesize the Nb-doped and LiNbO_(3)-coated LiNi_(0.83)Co_(0.12)Mn_(0.05)O_(2) cathode materials.The incorporation of LiNbO_(3) coating ...A one-step overall strategy from surface to bulk was proposed to simultaneously synthesize the Nb-doped and LiNbO_(3)-coated LiNi_(0.83)Co_(0.12)Mn_(0.05)O_(2) cathode materials.The incorporation of LiNbO_(3) coating can regulate the interface and facilitate the diffusion of Li-ions.Simultaneously,the stronger Nb—O bond can effectively suppress Li^(+)/Ni^(2+) cation mixing and strengthen the stability of crystal structure,which helps to mitigate the anisotropic variations of lattice parameters during Li^(+) de/intercalation.The results showed that the dual-modified materials exhibited good structural stability and distinguished electrochemical performance.The optimal NCM-Nb2 sample showed an excellent capacity retention of 90.78%after 100 cycles at 1C rate between 2.7 and 4.3 V,while only 67.90%for the pristine one.Meanwhile,it displayed a superior rate capability of 149.1 mA·h/g at the 10C rate.These results highlight the feasibility of one-step dual modification strategy to synchronously improve the electrochemical performance of Ni-rich layered oxide cathodes.展开更多
基金the Regional Innovation and Development Joint Fund of National Natural Science Foundation of China(No.U19A2018)the National Natural Science Foundation of China(No.21703191)+2 种基金Project of Innovation Team of the Ministry of Education,China(No.IRT_17R90)Hunan Provincial Natural Scientific Foundation of China(No.2019JJ50600)Outstanding Youth Project of Hunan Provincial Education Department,China(No.18B076).
文摘A one-step overall strategy from surface to bulk was proposed to simultaneously synthesize the Nb-doped and LiNbO_(3)-coated LiNi_(0.83)Co_(0.12)Mn_(0.05)O_(2) cathode materials.The incorporation of LiNbO_(3) coating can regulate the interface and facilitate the diffusion of Li-ions.Simultaneously,the stronger Nb—O bond can effectively suppress Li^(+)/Ni^(2+) cation mixing and strengthen the stability of crystal structure,which helps to mitigate the anisotropic variations of lattice parameters during Li^(+) de/intercalation.The results showed that the dual-modified materials exhibited good structural stability and distinguished electrochemical performance.The optimal NCM-Nb2 sample showed an excellent capacity retention of 90.78%after 100 cycles at 1C rate between 2.7 and 4.3 V,while only 67.90%for the pristine one.Meanwhile,it displayed a superior rate capability of 149.1 mA·h/g at the 10C rate.These results highlight the feasibility of one-step dual modification strategy to synchronously improve the electrochemical performance of Ni-rich layered oxide cathodes.