The effects of a pulsed magnetic field （PMF） on the microsegregation of solute elements during directional solidification of a Ni-based single crystal superalloy were experimentally investigated, and the results sho...The effects of a pulsed magnetic field （PMF） on the microsegregation of solute elements during directional solidification of a Ni-based single crystal superalloy were experimentally investigated, and the results show that the PMF significantly affects the microsegregation of Al, Ti, Co, Mo and W elements in the alloy. However, the distribution behavior differs for both positive and negative segregation elements. With the PMF, the microsegregation of negative segregation elements, Co and W, was restrained effectively, while that of positive segregation elements, A1, Ti and Mo, was aggravated. A segregation model was estab- lished to reveal the distribution mechanism of the elements with PME It is considered that, under the action of PME the jumping of solute atoms from the liquid phase to solid phase is hindered, but the jumping of solute atoms from the solid phase into liquid phase is promoted during solidification. As a result, the effective distribution coefficient of the solute atoms is reduced, which leads to the reduction of microsegregation of negative segregation elements and aggravation of microsegregation of positive segregation elements.展开更多
基金the financial support from the National Natural Science Foundation of China(No.51034012)the National Basic Research Program of China(No.2010CB631205)
文摘The effects of a pulsed magnetic field （PMF） on the microsegregation of solute elements during directional solidification of a Ni-based single crystal superalloy were experimentally investigated, and the results show that the PMF significantly affects the microsegregation of Al, Ti, Co, Mo and W elements in the alloy. However, the distribution behavior differs for both positive and negative segregation elements. With the PMF, the microsegregation of negative segregation elements, Co and W, was restrained effectively, while that of positive segregation elements, A1, Ti and Mo, was aggravated. A segregation model was estab- lished to reveal the distribution mechanism of the elements with PME It is considered that, under the action of PME the jumping of solute atoms from the liquid phase to solid phase is hindered, but the jumping of solute atoms from the solid phase into liquid phase is promoted during solidification. As a result, the effective distribution coefficient of the solute atoms is reduced, which leads to the reduction of microsegregation of negative segregation elements and aggravation of microsegregation of positive segregation elements.