The Tb3+/Sm3+ single-doped and co-doped glasses and glass ceramics containing YPO4 nanocrystals have been synthesized by melt quenching method. The structural and luminescent properties of these glass specimens were...The Tb3+/Sm3+ single-doped and co-doped glasses and glass ceramics containing YPO4 nanocrystals have been synthesized by melt quenching method. The structural and luminescent properties of these glass specimens were investigated. Under 375 nm wavelength excitation, the emission spectra combined with blue, green and red bands were observed, which achieved the white light emission. Moreover, the energy transfer between Tb3+ and Sm3+ ions was validated by decay lifetime measurement and energy level diagram. The color coordinates (x = 0.333, y = 0.333), correlated color temperature (5595 K) and the color render- ing index (Ra = 80.5) indicated that the glass ceramics were considered to be good lighting source. Hence, the YPO4-based Tb3+/Sm3+ co-doped glass ceramics can act as potential matrix materials for white light- emitting diodes under ultraviolet excitation.展开更多
The LiYF4 single crystals singly doped Ho3+ and co-doped Ho3+, Pr3+ ions were grown by a modified Bridgman method. The Judd-Ofelt strength parameters (Ω2, Ω4, Ω6) of No3+ were calculated according to the abso...The LiYF4 single crystals singly doped Ho3+ and co-doped Ho3+, Pr3+ ions were grown by a modified Bridgman method. The Judd-Ofelt strength parameters (Ω2, Ω4, Ω6) of No3+ were calculated according to the absorption spectra and the Judd-Ofelt theory, by which the radiative transition probabilities (A), fluorescence branching ratios (β) and radiative lifetime (τ rad) were obtained. The radiative lifetimes of 5/6 and 5/7 levels in Ho3+ (1 mol%):LiYF4 are 10.89 and 20.19 ms, respectively, while 9.77 and 18.50 ms in Ho3+/pr3+ doped crystals. Hence, the τ rad of 5/7 level decreases significantly by introduction of Pr3+ into Ho3+:LiYF4 crystal which is beneficial to the emission of 2.9 μm. The maximum emission cross section of Ho3+:LiYF4 crystal located at 2.05 μm calculated by McCumber theory is 0.51 ×10-20 cm2 which is compared with other crystals. The maximum emission cross section at 2948 nm in Ho3+/pr3+ co-doped LiYF4 crystal obtained by Fuchtbauer- Ladenburg theory is 0.68 × 10-20 cm2, and is larger than the value of 0.53 × 10-20 cm2 in Ho3+ singly doped LiYF4 crystal. Based on the absorption and emission cross section spectra, the gain cross section spectra were calculated. In the Ho3- ions singly doped LiYF4 crystal, the gain cross sections for 2.05 μm infrared emission becomes positive once the population inversion level reaches 30%. It means that the pump threshold for obtaining 2.05 μm laser is probably lower which is an advantage for Ho3+-doped LiYF4 2.05 μm infrared lasers. The calculated gain cross section for 2.9 μm mid-infrared emission does not become positive until the population inversion level reaches 40% in Ho3+/pr3+:LiYF4 crystal, but 50% in Ho3+ singly doped LiYF4 crystal, indicating that a low pumping threshold is achieved for the H03+:5/6 → 5/7 laser operation with the introduction of Pr3+ ions. It was also demonstrated that Pr3+ ion can deplete rapidly the lower laser Ho3+:5/7 level and has influence on the Ho3+:5/6 level. The Ho3+/pr3+:LiYF4 crystal may be a potential media for 2.9 μm mid-infrared laser.展开更多
基金supported by the National Natural Science Foundation of China(Nos.61275180 and 51472125)the K.C.Wong Magna Fund in Ningbo University
文摘The Tb3+/Sm3+ single-doped and co-doped glasses and glass ceramics containing YPO4 nanocrystals have been synthesized by melt quenching method. The structural and luminescent properties of these glass specimens were investigated. Under 375 nm wavelength excitation, the emission spectra combined with blue, green and red bands were observed, which achieved the white light emission. Moreover, the energy transfer between Tb3+ and Sm3+ ions was validated by decay lifetime measurement and energy level diagram. The color coordinates (x = 0.333, y = 0.333), correlated color temperature (5595 K) and the color render- ing index (Ra = 80.5) indicated that the glass ceramics were considered to be good lighting source. Hence, the YPO4-based Tb3+/Sm3+ co-doped glass ceramics can act as potential matrix materials for white light- emitting diodes under ultraviolet excitation.
基金supported by the National Natural Science Foundation of China(Grant Nos.51272109 and 50972061)the Natural Science Foundation of Zhejiang Province(Grant Nos.R4100364)the Natural Science Foundation of Ningbo City(Grant No.2012A610115)
文摘The LiYF4 single crystals singly doped Ho3+ and co-doped Ho3+, Pr3+ ions were grown by a modified Bridgman method. The Judd-Ofelt strength parameters (Ω2, Ω4, Ω6) of No3+ were calculated according to the absorption spectra and the Judd-Ofelt theory, by which the radiative transition probabilities (A), fluorescence branching ratios (β) and radiative lifetime (τ rad) were obtained. The radiative lifetimes of 5/6 and 5/7 levels in Ho3+ (1 mol%):LiYF4 are 10.89 and 20.19 ms, respectively, while 9.77 and 18.50 ms in Ho3+/pr3+ doped crystals. Hence, the τ rad of 5/7 level decreases significantly by introduction of Pr3+ into Ho3+:LiYF4 crystal which is beneficial to the emission of 2.9 μm. The maximum emission cross section of Ho3+:LiYF4 crystal located at 2.05 μm calculated by McCumber theory is 0.51 ×10-20 cm2 which is compared with other crystals. The maximum emission cross section at 2948 nm in Ho3+/pr3+ co-doped LiYF4 crystal obtained by Fuchtbauer- Ladenburg theory is 0.68 × 10-20 cm2, and is larger than the value of 0.53 × 10-20 cm2 in Ho3+ singly doped LiYF4 crystal. Based on the absorption and emission cross section spectra, the gain cross section spectra were calculated. In the Ho3- ions singly doped LiYF4 crystal, the gain cross sections for 2.05 μm infrared emission becomes positive once the population inversion level reaches 30%. It means that the pump threshold for obtaining 2.05 μm laser is probably lower which is an advantage for Ho3+-doped LiYF4 2.05 μm infrared lasers. The calculated gain cross section for 2.9 μm mid-infrared emission does not become positive until the population inversion level reaches 40% in Ho3+/pr3+:LiYF4 crystal, but 50% in Ho3+ singly doped LiYF4 crystal, indicating that a low pumping threshold is achieved for the H03+:5/6 → 5/7 laser operation with the introduction of Pr3+ ions. It was also demonstrated that Pr3+ ion can deplete rapidly the lower laser Ho3+:5/7 level and has influence on the Ho3+:5/6 level. The Ho3+/pr3+:LiYF4 crystal may be a potential media for 2.9 μm mid-infrared laser.