Silicone-coated polyimide films deposited by surface dielectric barrier discharges

Hybrid dielectric barrier discharges are investigated for plasma generated on the surface of a dielectric layer, where two conducting electrodes of high voltage and ground are formulated on the upper and bottom surfaces. Using a flexible thin polyimide-film of a thickness ranging from 25 to 125 μm, a plasma is generated with a voltage of about 1 kV and a frequency of 40 kHz.However, the surface of the dielectric layer was etched through a chemical reaction involving plasma oxygen radical species, and thus the polyimide films failed readily, resulting in dielectric breakdown within short operating time ranging from a few minutes to several tens of minutes,based on the film thicknesses of 25 μm and 125 μm, respectively. These plasma erosions were prevented by coating the polyimide surface with a 25 μm thick silicone paste. The siliconecoated film surface was then reinforced remarkably against plasma erosion as the organic polymer was vulnerable to chemical reaction of the plasma species, while the inorganic silicone exhibited a high chemical resistance against plasma erosion.

Adsorption of phosphate on magnetite-enriched particles (MEP) separated from the mill scale

Phosphate is a major pollutant in water, causing serious environmental and health consequences. In present study, the phosphate adsorption on novel magnetite-enriched particles (MEP) was comprehensively investigated. A new method and device were introduced for the separation of MEP from the mill scale at low magnetic intensity. Particles were characterized with different techniques such as XRD, XRF, SEM and EDS. The XRD and XRF analysis of MEP identified the dominant existence of crystalline magnetite. Furthermore, the morphological analysis of MEP confirmed the agglomerate porous morphology of magnetite. Oxygen and iron, the main constituents of magnetite were acknowledged during the elemental analysis using EDS. The phosphate adsorption on MEP is well explained using various isotherm and kinetic models, exhibiting the monolayer adsorption of phosphate on the surface of MEP. The maximum adsorption capacity was determined 6.41 mg/g. Based on particle size (45–75 and 75–150 μm) and empty bed contact time (1 and 2 h), four columns were operated for 54 days. MEP were appeared successful to remove all phosphate concentration from the column influent having 2 mg/L concentration. The operated column reactors were successfully regenerated with alkaline solution. The results indicated potential for practical application of the MEP for phosphate removal.