Microbiologically influenced corrosion resistance enhancement of coppercontaining high entropy alloy Fe_(x)Cu_(1−x)CoNiCrMn against Pseudomonas aeruginosa

To enhance the microbiologically influenced corrosion(MIC)resistance of FeCoNiCrMn high entropy alloy(HEAs),a series of Fe_(x)Cu_((1−x))CoNiCrMn(x=1,0.75,0.5,and 0.25)HEAs were prepared.Microstructural characteristics,corrosion behavior(morphology observation and electrochemical properties),and antimicrobial performance of Fe_(x)Cu_((1−x))CoNiCrMn HEAs were evaluated in a medium inoculated with typical corrosive microorganism Pseudomonas aeruginosa.The aim was to identify copper-containing FeCoNiCrMn HEAs that balance corrosion resistance and antimicrobial properties.Results revealed that all Fe_(x)Cu_((1−x))CoNiCrMn(x=1,0.75,0.5,and 0.25)HEAs exhibited an FCC(face centered cubic)phase,with significant grain refinement observed in Fe_(0.75)Cu_(0.25)CoNiCrMn HEA.Electrochemical tests indicated that Fe_(0.75)Cu_(0.25)CoNiCrMn HEA demonstrated lower corrosion current density(i_(corr))and pitting potential(E_(pit))compared to other Fe_(x)Cu_((1−x))CoNiCrMn HEAs in P.aeruginosa-inoculated medium,exhibiting superior resistance to MIC.Anti-microbial tests showed that after 14 d of immersion,Fe_(0.75)Cu_(0.25)CoNiCrMn achieved an antibacterial rate of 89.5%,effectively inhibiting the adhesion and biofilm formation of P.aeruginosa,thereby achieving resistance to MIC.

Microbiologically Influenced Corrosion Behavior of Fe_(40)(CoCrMnNi)_(60) and Fe_(60)(CoCrMnNi)_(40) Medium Entropy Alloys in the Presence of Pseudomonas Aeruginosa

In this work,the microbiologically influenced corrosion(MIC)of Fe_(40)(CoCrMnNi)_(60) and Fe_(60)(CoCrMnNi)_(40) medium entropy alloys(MEAs)induced by Pseudomonas aeruginosa(P.aeruginosa)was investigated.Corrosion behaviors during 14 days of immersion in sterile and P.aeruginosa-inoculated culture media are presented.Under sterile conditions,both MEAs exhibited good corrosion resistance against the culture medium solution.In the presence of P.aeruginosa,the pitting corrosion of MEAs was promoted.The results of inductively coupled plasma‒mass spectrometry(ICP‒MS)and potentiodynamic polarization tests showed that the presence of P.aeruginosa promoted the selective dissolution of passive film and accelerated the corrosion of MEAs.The results of X-ray photoelectron spectroscopy(XPS)and Mott-Schottky measurements further demonstrated the degradation effect of P.aeruginosa on the passive film.Compared with Fe_(60)(CoCrMnNi)_(40),Fe_(40)(CoCrMnNi)_(60) manifested better resistance to the MIC caused by P.aeruginosa,which may be attributed to more Cr oxides and fewer Fe oxides of the passive film.

Methanogenic archaea and sulfate reducing bacteria induce severe corrosion of steel pipelines after hydrostatic testing

Complex interactions within a microbial consortium can induce severe corrosion in oil pipelines.This study investigated the mechanism of microbiologically influenced corrosion(MIC)that led to failure of X52 steel pipelines after hydrostatic testing.Laboratory hydrostatic testing with untreated lake water and underground water were used to simulate and study the events that led to the actual corrosion.Biofilm analysis,weight loss,and several electrochemical measurements demonstrated rapid corrosion rates after hydrostatic testing.Analysis of microbial community structures revealed that methanogenic archaea and sulfate reducing bacteria(SRB),introduced by the hydrotest water,formed corrosive biofilms on X52 steel coupon surfaces that induced severe pitting.

Microbiologically influenced corrosion of 304 stainless steel by halophilic archaea Natronorubrum tibetense

The corrosion behavior of 304 stainless steel(SS)in the presence of aerobic halophilic archaea Natronorubrum tibetense was investigated.After 14 days of immersion,no obvious pitting pit was observed on the SS surface in the sterile medium.By contrast,the SS exhibited serious pitting corrosion with the largest pit depth of 5.0μm in the inoculated medium after 14 days.The results of electrochemical tests showed that the barrier property of the passive film decreased faster in the inoculated medium.The X-ray photoelectron spectroscopy results indicated that the detrimental Fe2+and Cr6+increased in the passive film under the influence of archaea N.tibetense,which resulted in the accelerated deterioration of passive film and promoted the pitting corrosion.Combined with the energy starvation tests,the microbiologically influenced corrosion mechanism of 304 SS caused by halophilic archaea N.tibetense was discussed finally.

Mechanically durable antibacterial nanocoatings based on zwitterionic copolymers containing dopamine segments

Developing an effective and durable antibacterial surface is important for surgical tools and biomedical implants.In this work,a zwitterionic copolymer containing catechol groups as biomimetic anchoring segments was coated onto 316 L stainless steel via drop-casting.Energy-dispersive X-ray spectroscopy(EDS)and water contact angle(WCA)measurements indicated that the coatings made of the copolymers containing zwitterionic and dopamine segments at the molar ratios of 8:2 and 6:4 exhibited stronger stability and mechanical durability than the one at 9:1 after inducing tape-peeling and ultrasonication damage.The mechanically durable nanocoatings exhibited excellent antibacterial performance against Staphylococcus aureus and Escherichia coli in a period of 3 days.The nanocoatings with zwitterionic and dopamine segments at the molar ratio of 8:2 were further evaluated and demonstrated durable antibacterial performance after tape-peeling and ultrasonication treatments.