Spectral features and antibacterial properties of Cu-doped ZnO nanoparticles prepared by sol-gel method

Zn（1-x）Cux O（x=0.00, 0.01, 0.03, and 0.05） nanoparticles are synthesized via the sol-gel technique using gelatin and nitrate precursors. The impact of copper concentration on the structural, optical, and antibacterial properties of these nanoparticles is demonstrated. Powder x-ray diffraction investigations have illustrated the organized Cu doping into ZnO nanoparticles up to Cu concentration of 5%（x = 0.05）. However, the peak corresponding to CuO for x= 0.01 is not distinguishable. The images of field emission scanning electron microscopy demonstrate the existence of a nearly spherical shape with a size in the range of 30–52 nm. Doping Cu creates the Cu–O–Zn on the surface and results in a decrease in the crystallite size. Photoluminescence and absorption spectra display that doping Cu causes an increment in the energy band gap. The antibacterial activities of the nanoparticles are examined against Escherichia coli（Gram negative bacteria）cultures using optical density at 600 nm and a comparison of the size of inhibition zone diameter. It is found that both pure and doped ZnO nanoparticles indicate appropriate antibacterial activity which rises with Cu doping.

Effects of Mg substitution on the structural and magnetic properties of Co0.5Ni（0.5-x）MgxFe2O4 nanoparticle ferrites

In this study, nanocrystalline Co-Ni-Mg ferrite powders with composition Coo.5Nio.5-xMgxFe2O4 are successfully synthesized by the co-precipitation method. A systematic investigation on the structural, morphological and magnetic properties of un-doped and Mg-doped Co-Ni ferrite nanoparticles is carried out. The prepared samples are characterized using x-ray diffraction （XRD） analysis, Fourier transform infrared spectroscopy （FTIR）, field emission scanning electron microscopy （FESEM）, and vibrating sample magnetometry （VSM）. The XRD analyses of the synthesized samples confirm the formation of single-phase cubic spinel structures with crystallite sizes in a range of - 32 nm to - 36 nm. The lat- tice constant increases with increasing Mg content. FESEM images show that the synthesized samples are homogeneous with a uniformly distributed grain. The results of IR spectroscopy analysis indicate the formation of functional groups of spinel ferrite in the co-precipitation process. By increasing Mg2- substitution, room temperature magnetic measurement shows that maximum magnetization and coercivity increase from - 57.35 emu/g to - 61.49 emu/g and - 603.26 Oe to 684.11 Oe （l Oe = 79.5775 A.m-l）, respectively. The higher values of magnetization Ms and Mr suggest that the opti- mum composition is Co0.5Ni0.4Mg0.1Fe204 that can be applied to high-density recording media and microwave devices.