During the welding of AZ91 cast alloy,the presence of eutectic β-Mg17Al12 phase results in constitutional liquation in the original interdendritic regions and in the formation of a partially melted zone(PMZ). In this...During the welding of AZ91 cast alloy,the presence of eutectic β-Mg17Al12 phase results in constitutional liquation in the original interdendritic regions and in the formation of a partially melted zone(PMZ). In this study,gas tungsten arc welding(GTAW) and partial melting(simulated using furnace,salt bath and Gleeble) experiments were conducted. The results show that practically there would not be a critical heating rate during the welding to prevent constitutional liquation. The gradual change of the re-solidification microstructure within PMZ from base metal side to weld metal side was characterized. A sharp transition from base metal to PMZ has been observed. It is found that the original partially divorced eutectic has become a more regular eutectic in most of the PMZ,although close to the fusion boundary the re-solidified eutectic is again a more divorced one. Proceeding the eutectic re-solidification,α-Mg re-solidified with a cellular growth resulting in a serrated interface. The morphological change affected by the peak temperature and cooling rate will be presented and explained.展开更多
文摘During the welding of AZ91 cast alloy,the presence of eutectic β-Mg17Al12 phase results in constitutional liquation in the original interdendritic regions and in the formation of a partially melted zone(PMZ). In this study,gas tungsten arc welding(GTAW) and partial melting(simulated using furnace,salt bath and Gleeble) experiments were conducted. The results show that practically there would not be a critical heating rate during the welding to prevent constitutional liquation. The gradual change of the re-solidification microstructure within PMZ from base metal side to weld metal side was characterized. A sharp transition from base metal to PMZ has been observed. It is found that the original partially divorced eutectic has become a more regular eutectic in most of the PMZ,although close to the fusion boundary the re-solidified eutectic is again a more divorced one. Proceeding the eutectic re-solidification,α-Mg re-solidified with a cellular growth resulting in a serrated interface. The morphological change affected by the peak temperature and cooling rate will be presented and explained.