（Cu-Ni）/（10NiO-90NiFe204） cermet inert anodes containing metal Cu-Ni0, 5, 10, 15 and 20 wt pct were prepared and their corrosion resistance to Na3AlF6-Al2O3 melts was investigated. The results indicate that the co...（Cu-Ni）/（10NiO-90NiFe204） cermet inert anodes containing metal Cu-Ni0, 5, 10, 15 and 20 wt pct were prepared and their corrosion resistance to Na3AlF6-Al2O3 melts was investigated. The results indicate that the content of metal Cu-Ni has little effect on the steady-state concentration of Ni in the electrolyte and the values could not be used to effectively differentiate their corrosion resistance. The steady-state concentration of Fe decreases from 304×10^-6 to 168×10^-6 and that of Cu increases from 21×10^-6 to 71×10^-6 with the content of metal Cu-Ni increasing from 0 to 20 wt pct. Post-examination shows that metallic phase Cu-Ni is corroded preferentially during electrolysis and many pores are left at the anode surface. Considering the corrosion resistance and electrical conductivity, the cermet containing metal Cu-Ni 5 wt pct should be selected and studied further.展开更多
基金financial support from National Basic Research Program of China(No.2005CB623703)National Natural Science Foundation of China(No.50474051).
文摘（Cu-Ni）/（10NiO-90NiFe204） cermet inert anodes containing metal Cu-Ni0, 5, 10, 15 and 20 wt pct were prepared and their corrosion resistance to Na3AlF6-Al2O3 melts was investigated. The results indicate that the content of metal Cu-Ni has little effect on the steady-state concentration of Ni in the electrolyte and the values could not be used to effectively differentiate their corrosion resistance. The steady-state concentration of Fe decreases from 304×10^-6 to 168×10^-6 and that of Cu increases from 21×10^-6 to 71×10^-6 with the content of metal Cu-Ni increasing from 0 to 20 wt pct. Post-examination shows that metallic phase Cu-Ni is corroded preferentially during electrolysis and many pores are left at the anode surface. Considering the corrosion resistance and electrical conductivity, the cermet containing metal Cu-Ni 5 wt pct should be selected and studied further.