导电高聚物在循环载荷作用下的力/电性能研究

以聚丙烯(PP)为基体、导电炭黑(CB)为填料,通过熔融共混、注塑成型的方法制备导电复合材料。测定在恒应力幅值条件下,加载频率为1 Hz时,不同填料含量的导电高聚物在循环压缩载荷作用下的力/电性能。结果表明:随循环周数增加,滞后环变小,塑性应变累积发生棘轮效应,随填料含量的增加,呈现出明显的疏-密特点,后期基本趋于重合,应变随填料含量增加而增加。当导电填料含量在逾渗区附近,导电通道相对脆弱,电性能不稳定;稍高于逾渗区,循环初始阶段,有微小波动,循环载荷后期基本趋于稳定;远高于逾渗区时,表现出良好的电性能的稳定性。通过扫描电子显微镜观察了导电填料的分布状况。

Studies on the Syntheses and Biological Activities of 3-Aryl-6-(1,1'-biphenyl-4-yl)-7H-1,2,4-triazolo[3,4-b][1,3,4]thiadiazines

A series of novel 3-aryl-6-(1,1’-biphenyl-4-yl)-7H-1,2,4-triazolothiadiazines was synthesized by means of the reactions between 3-aryl-4-amino-5-mercapto-1,2,4-triazoles and 2-bromo-4’-phenylacetophenone. The structures of all the title compounds have been confirmed by virtue of elemental analysis, IR, 1H NMR, 13C NMR and mass spectra. The characteristics of 13C NMR peaks of the compounds were investigated. The plant growth regulating effects of those compounds were also determined.

基于纳米压痕技术的炭黑/聚丙烯复合材料力学性能研究

利用纳米压痕技术对炭黑填充聚丙烯基(CB/PP)复合材料的弹性模量、硬度及蠕变行为等力学性能进行了实验研究。结果表明,炭黑颗粒对CB/PP复合材料具有强化作用,随着炭黑含量的增加,复合材料的弹性模量和硬度增加。实验得出了纯PP及CB/PP复合材料蠕变应力指数和蠕变特征松弛时间,结果表明炭黑含量的增加增大了复合材料的蠕变应力指数,并且提高了硬度和抗疲劳性能。同时炭黑含量增加,复合材料的蠕变特征松弛时间减小,表明炭黑颗粒有效阻碍了聚合物分子链的移动。

硅烷封端聚氨酯预聚体的合成研究

以聚醚二元醇、二异氰酸酯为主要原料合成了硅烷封端聚氨酯预聚体,使用合成得到的预聚体制备了硅烷封端聚氨酯密封胶并对其性能进行了考察。研究了二异氰酸酯类型,NCO/OH比例,反应温度,扩链剂类型及封端剂类型对硅烷封端聚氨酯(SPU)的影响。结果表明:使用两种混合二异氰酸酯,NCO∶OH=1.3～1.5,二甘醇作为扩链剂,γ-巯丙基三甲基硅烷(KH590)作为封端剂,反应温度85℃制备得到较理想的预聚体,可使硅烷封端聚氨酯密封胶拉伸强度达到1.78MPa,断裂伸长率达到490%。