A magnetic nanoparticles-loaded polymeric nanocarrier was developed. Amphiphilic copolymer, methoxy polyethylene glycol-poly（D,L-lactide-co-glycolide）（MPEG-PLGA） could self-assemble to form nanomicelle with the he...A magnetic nanoparticles-loaded polymeric nanocarrier was developed. Amphiphilic copolymer, methoxy polyethylene glycol-poly（D,L-lactide-co-glycolide）（MPEG-PLGA） could self-assemble to form nanomicelle with the help of emulsion-solvent evaporation technique. This nanocarrier with core-shell structure was loaded with magnetic iron oxide nanoparticles（IONPs） and anticancer drug paclitaxel（PTX）. The hydrodynamic diameter of IONPs-PTX-loaded nanocarrier showed an average size of 110 nm with a polydispersity index（PDI） of 0.136, and its zeta potential was （-4.76±0.36） mV. The drug-loading content and encapsulation efficiency were 4.47% and 31.28%, respectively. In vitro drug release experiment was performed and a sustained release profile was observed. 3-（4,5-Dimethyl-2-thiazolyl）-2,5-diphenyl-2-H-tetrazolium bromide（MTT） assay indicated that IONPs-PTX-loaded nanocarrier showed comparable cytotoxicity with free paclitaxel. When an external magnetic field was applied, the nanocarrier significantly localized at the target area, demonstrating that the nanocarrier could be used for potential magnetic targeted drug delivery.展开更多
基金Supported by the National Natural Science Foundation of China（Nos.81271697, 81571791, 31571017, 81171431）, the Specialized Research Fund for the Doctoral Program of Higher Education of China（Nos.20100061120077, 20120061110021）, the Social Development Project of Science and Technology Department of Jilin Province, China（Nos.20120967, YYZX201264, 20130206069GX） and the ＂Significant New Drug Creation＂ Science and Technology Major Program of China （No.2012ZX09503001-003）.
文摘A magnetic nanoparticles-loaded polymeric nanocarrier was developed. Amphiphilic copolymer, methoxy polyethylene glycol-poly（D,L-lactide-co-glycolide）（MPEG-PLGA） could self-assemble to form nanomicelle with the help of emulsion-solvent evaporation technique. This nanocarrier with core-shell structure was loaded with magnetic iron oxide nanoparticles（IONPs） and anticancer drug paclitaxel（PTX）. The hydrodynamic diameter of IONPs-PTX-loaded nanocarrier showed an average size of 110 nm with a polydispersity index（PDI） of 0.136, and its zeta potential was （-4.76±0.36） mV. The drug-loading content and encapsulation efficiency were 4.47% and 31.28%, respectively. In vitro drug release experiment was performed and a sustained release profile was observed. 3-（4,5-Dimethyl-2-thiazolyl）-2,5-diphenyl-2-H-tetrazolium bromide（MTT） assay indicated that IONPs-PTX-loaded nanocarrier showed comparable cytotoxicity with free paclitaxel. When an external magnetic field was applied, the nanocarrier significantly localized at the target area, demonstrating that the nanocarrier could be used for potential magnetic targeted drug delivery.