透射电镜在磁性斯格明子领域的应用

介绍了透射电镜研究磁性斯格明子的原理,以及利用透射电镜结合温度、电流、磁场等外场原位技术协同调控拓扑磁畴结构的方法。该调控方法不仅可以高分辨率表征静态磁性斯格明子的自旋组态,还可以原位、实时展示外场调控的动力学过程,具有在实空间、原位、实时、高分辨率解析斯格明子演变的优势。综述了该方法在中心对称块体、对称性破缺材料和铁磁薄膜等3个主要磁性材料体系中,对拓扑磁畴结构的调控作用。获得了宽温区、高密度、零场非易失性的斯格明子,分析了拓扑磁畴结构的温度稳定性、高密度和非易失性,揭示了磁各向异性对斯格明子自旋组态和密度影响的物理机制和规律。透射电镜所具有的纳米尺度高分辨分析磁畴结构以及原位外场调控的优势将有助于磁涡旋、磁麦纫、磁性斯格明子、磁泡等多种新型拓扑磁畴结构的分析和探索。

Giant Magnetoresistance Effect in Melt Spun CoCu granular Alloys

granular magnetic Co_(x)Cu_(1-x)(x=0.05-0.5)alloy ribbons were prepared by melt spinning method,and the structural,magnetotransport,magnetic properties and the effects of annealing on these properties were studied by x-ray diffraction,vibrating sample magnetometer,magnetoresistance measurement at room temperature.Giant magnetoresistance was observed over a broad range of Co concentrations with a maximum magnetoresistance(MR)ratio of 7.8%(at x=0.20 and 500℃ annealing)under a magnetic field of 20kOe.The MR ratio increases with the annealing temperature and reaches a maximum at about 500℃ and then drops.The dependence of MR and magnetization on magnetic field for various granule parameters were studied by controlling the nucleation and growth of Co granules.

旋甩快淬带ErCoSi的各向异性磁热效应

磁制冷技术的关键在于磁热效应材料的发展。具有各向异性磁热效应的新型磁制冷材料可以用于旋转磁制冷技术而被广泛研究。研究了ErCoSi旋甩快淬带化合物的磁性、磁热效应及磁各向异性。在T_(c)=5.5 K处发生了铁磁(FM)到顺磁(PM)的二级相变。通过分析5 m/s-ErCoSi快淬带在磁场∥和⊥横截面的两个方向的等温磁化曲线、磁熵变和磁制冷能力可知,在μ0H=0~5 T的磁场变化时,磁场∥和⊥快淬带横截面的最大磁熵变值-ΔS M分别为17.5 J·kg^(-1)k^(-1)和12 J·kg^(-1)k^(-1);制冷能力分别可达230 J·kg^(-1)和120 J·kg^(-1).表明5 m/s-ErCoSi快淬带具有大的磁热效应和明显的磁各向异性,有望实现旋转样品磁制冷技术.