The effects of acetylene black powder surface free energy on air electrode electrochemical performance and lifetime were studied.The acetylene black was immersed in 30%H_(2)O_(2)at room temperature and the changes of ...The effects of acetylene black powder surface free energy on air electrode electrochemical performance and lifetime were studied.The acetylene black was immersed in 30%H_(2)O_(2)at room temperature and the changes of functional groups and surface free energy were investigated by X-ray Photoelectron Spectroscopy(XPS)and powder contact angle(CA).The air electrode performance was characterized by the potential polarization curves and the lifetime was measured by constant-current discharge.It shows that,its surface free energy is the lowest when the acetylene black is immersed in H_(2)O_(2)for 240 h.The polarization potential of the air electrode prepared by the pretreated acetylene black is 0.25 V(vs.Hg/HgO),0.21 V lower than the air electrode with untreated acetylene black when the working current density is 100 mA·cm^(-1).And its lifetime is over 800 h at 80 mA·cm^(-1).The pretreatment of acetylene black for proper time by H_(2)O_(2)is favorable for the stability of the tri-phase reaction interface of air electrode and improvement of its performance.展开更多
基金This work was financially supported by the Key Technologies R&D Programme of Hebei Province(401073).
文摘The effects of acetylene black powder surface free energy on air electrode electrochemical performance and lifetime were studied.The acetylene black was immersed in 30%H_(2)O_(2)at room temperature and the changes of functional groups and surface free energy were investigated by X-ray Photoelectron Spectroscopy(XPS)and powder contact angle(CA).The air electrode performance was characterized by the potential polarization curves and the lifetime was measured by constant-current discharge.It shows that,its surface free energy is the lowest when the acetylene black is immersed in H_(2)O_(2)for 240 h.The polarization potential of the air electrode prepared by the pretreated acetylene black is 0.25 V(vs.Hg/HgO),0.21 V lower than the air electrode with untreated acetylene black when the working current density is 100 mA·cm^(-1).And its lifetime is over 800 h at 80 mA·cm^(-1).The pretreatment of acetylene black for proper time by H_(2)O_(2)is favorable for the stability of the tri-phase reaction interface of air electrode and improvement of its performance.