The fretting wear behavior of plasma spraying CoCrW and Cr3C2-NiCr coatings were investigated. The results showed both plasma spraying coatings were inferior to K417 nickel superalloy in the fretting wear resistance. ...The fretting wear behavior of plasma spraying CoCrW and Cr3C2-NiCr coatings were investigated. The results showed both plasma spraying coatings were inferior to K417 nickel superalloy in the fretting wear resistance. The characterized fatigue delamination of the plasma sprayed coatings was evidently different from that of the homogeneous materials. The lamellar cohesion, oxide inclusions and porosity were critical factors that controlled the fretting wear resistance. In the view of contact mechanics, the fretting wear behavior of plasma spraying coatings was characterized.展开更多
In order to well design tribosystems of dental CAD-CAM restorations, an understanding of the tribological mechanisms of dental machinable porcelain are essential. The friction and wear behavior of new generation indus...In order to well design tribosystems of dental CAD-CAM restorations, an understanding of the tribological mechanisms of dental machinable porcelain are essential. The friction and wear behavior of new generation industrially prefabricated Cerec Vitablocs Mark II against uniform Si3N4 ball has been performed using a small amplitude reciprocating apparatus under simulating oral conditions. The loads of 10-40 N, reciprocating amplitudes of 100-500 urn, frequencies of 1-4 Hz and two lubrications (no / artificial saliva lubrication) were selected. Tests lasting up to 10 000 cycles were conducted. The results show that Cerec Vitablocs Mark II record a friction coefficient of 0.55-0.84. Artificial saliva plays a lubricant effect during wear process. Among three parameters of the test on friction coefficient and wear depth of dental machinable porcelains, the load effect is prominent. Abrasive wear is the main wear mechanism, but brittle cracks and delamination are more popular especially under unlubricated friction.展开更多
文摘The fretting wear behavior of plasma spraying CoCrW and Cr3C2-NiCr coatings were investigated. The results showed both plasma spraying coatings were inferior to K417 nickel superalloy in the fretting wear resistance. The characterized fatigue delamination of the plasma sprayed coatings was evidently different from that of the homogeneous materials. The lamellar cohesion, oxide inclusions and porosity were critical factors that controlled the fretting wear resistance. In the view of contact mechanics, the fretting wear behavior of plasma spraying coatings was characterized.
基金supported by grant 50305030 from the Chinese Natural Science Foundationgrant 2003033526 from China Postdoctoral Science Foundationgrant 03SG022 from Sicence an d Technology Office of Sichuan Province.
文摘In order to well design tribosystems of dental CAD-CAM restorations, an understanding of the tribological mechanisms of dental machinable porcelain are essential. The friction and wear behavior of new generation industrially prefabricated Cerec Vitablocs Mark II against uniform Si3N4 ball has been performed using a small amplitude reciprocating apparatus under simulating oral conditions. The loads of 10-40 N, reciprocating amplitudes of 100-500 urn, frequencies of 1-4 Hz and two lubrications (no / artificial saliva lubrication) were selected. Tests lasting up to 10 000 cycles were conducted. The results show that Cerec Vitablocs Mark II record a friction coefficient of 0.55-0.84. Artificial saliva plays a lubricant effect during wear process. Among three parameters of the test on friction coefficient and wear depth of dental machinable porcelains, the load effect is prominent. Abrasive wear is the main wear mechanism, but brittle cracks and delamination are more popular especially under unlubricated friction.