Structure evolution of an Al-Zn wrought alloy in remelting processing in thestrain induced melt activated (SIMA) serai-solid procedure was observed, and effects of factors, theremelting temperature, the holding time, ...Structure evolution of an Al-Zn wrought alloy in remelting processing in thestrain induced melt activated (SIMA) serai-solid procedure was observed, and effects of factors, theremelting temperature, the holding time, and the compression strain, on structures and grain sizesof the alloy were investigated. The results show that (1) the proper temperature of remelting is inthe range of 610 to 615℃; (2) the grain size in specimen with greater compression strain is smallerthan that with smaller compression strain in condition of the same remelting temperature andholding time, and the grain size in local area with great local equivalent strain is smaller thanthat with small one; (3) liquid occurs in form of cluster in matrix during remelting and itsquantity increases with remelting time increasing; liquid in specimen with great compression strainoccurs earlier than that with small one, and quantity of liquid in the center of specimen withgreater local equivalent strain is greater than that in the two ends of it; (4) distortion energyafter deforming in matrix of the alloy is the significant factor to activate melting of matrix atlocal area with great local equivalent strain.展开更多
文摘Structure evolution of an Al-Zn wrought alloy in remelting processing in thestrain induced melt activated (SIMA) serai-solid procedure was observed, and effects of factors, theremelting temperature, the holding time, and the compression strain, on structures and grain sizesof the alloy were investigated. The results show that (1) the proper temperature of remelting is inthe range of 610 to 615℃; (2) the grain size in specimen with greater compression strain is smallerthan that with smaller compression strain in condition of the same remelting temperature andholding time, and the grain size in local area with great local equivalent strain is smaller thanthat with small one; (3) liquid occurs in form of cluster in matrix during remelting and itsquantity increases with remelting time increasing; liquid in specimen with great compression strainoccurs earlier than that with small one, and quantity of liquid in the center of specimen withgreater local equivalent strain is greater than that in the two ends of it; (4) distortion energyafter deforming in matrix of the alloy is the significant factor to activate melting of matrix atlocal area with great local equivalent strain.