AgNbO_(3)(AN)and modified AgNbO_(3) have been extensively investigated as promising lead-free antiferroelectric(AFE)energy storage materials.Previous studies have focused mainly on the use of an ion dopant at the A/B ...AgNbO_(3)(AN)and modified AgNbO_(3) have been extensively investigated as promising lead-free antiferroelectric(AFE)energy storage materials.Previous studies have focused mainly on the use of an ion dopant at the A/B site to obtain a stabilized AFE phase;however,simultaneous improvements in the recoverable energy storage density(Wrec)and efficiency(n)are stll difficult to realize.Herein,we innovatively constructed a AgNbO_(3)-NaNbO_(3)-(Sr_(0.7)Bi_(0.2))TiO_(3)(AN-NN-SBT)ternary solid solution to achieve a relaxor AFE in AgNbO_(3)-based materials.The coexistence of antiferroelectric(M3)and paraelectric(O)phases in 0.8(0.7AgNbO_(3)-0.3NaNbO_(3))-0.2(Sro.7Bio.2)TiO_(3) confirms the successful realization of a relaxor AFE,attributed to multiple ion occupation at the A/B sites.Consequently,a high Wrec of 7.53 J.cm^(-3) and n of 74.0% are acquired,together with superior stability against various temperatures,frequencies,and cycling numbers.Furthermore,a high power density(298.7 MW·cm^(-3))and fast discharge speed(41.4 ns)are also demonstrated for the AgNbO_(3)-based relaxor AFE.This work presents a promising energy storage AgNbO_(3)-based ternary solid solution and proposes a novel strategy for AgNbO_(3)-based energy storage via the design of relaxor AFE materials.展开更多
基金This work was supported by the National Natural Science Foundation of China(Nos.12204503 and U2002217)the Key Research Program of the Chinese Academy of Sciences(No.ZDRW-CN-2021-3-1-18)+2 种基金the Shanghai Pujiang Program(No.22PJD085)the Natural Science Foundation of Shanghai(No.23ZR1472400)the Young Elite Scientists Sponsorship Program by the China Association for Science and Technology(No.YESS20210265).
文摘AgNbO_(3)(AN)and modified AgNbO_(3) have been extensively investigated as promising lead-free antiferroelectric(AFE)energy storage materials.Previous studies have focused mainly on the use of an ion dopant at the A/B site to obtain a stabilized AFE phase;however,simultaneous improvements in the recoverable energy storage density(Wrec)and efficiency(n)are stll difficult to realize.Herein,we innovatively constructed a AgNbO_(3)-NaNbO_(3)-(Sr_(0.7)Bi_(0.2))TiO_(3)(AN-NN-SBT)ternary solid solution to achieve a relaxor AFE in AgNbO_(3)-based materials.The coexistence of antiferroelectric(M3)and paraelectric(O)phases in 0.8(0.7AgNbO_(3)-0.3NaNbO_(3))-0.2(Sro.7Bio.2)TiO_(3) confirms the successful realization of a relaxor AFE,attributed to multiple ion occupation at the A/B sites.Consequently,a high Wrec of 7.53 J.cm^(-3) and n of 74.0% are acquired,together with superior stability against various temperatures,frequencies,and cycling numbers.Furthermore,a high power density(298.7 MW·cm^(-3))and fast discharge speed(41.4 ns)are also demonstrated for the AgNbO_(3)-based relaxor AFE.This work presents a promising energy storage AgNbO_(3)-based ternary solid solution and proposes a novel strategy for AgNbO_(3)-based energy storage via the design of relaxor AFE materials.