The oxidation behavior of 0. 8% La2O3- Mo5Si3/MoSi2 composites at 1200℃ in air was investigated. The results reveal that the oxidation resistance of the material with 0. 8% La2O3 and Mo5Si3 is impaired. The oxidation...The oxidation behavior of 0. 8% La2O3- Mo5Si3/MoSi2 composites at 1200℃ in air was investigated. The results reveal that the oxidation resistance of the material with 0. 8% La2O3 and Mo5Si3 is impaired. The oxidation resistance is decreased with increasing Mo5Si3 content. The mass loss follows a linear law in the initial oxidation. With oxidation time prolonging, a continuous and dense oxidation scale prevents oxygen from diffusing increasing when and leads to mass change a Mo5Si3 content is less than 30%. However, the composite shows ＂PEST＂ with the addition of 40% Mo5Si3. With increasing Mo5Si3 content, the oxidation resistance of 0.8% La2O3- Mo5Si3/MoSi2 decreases. This attributes to the poor oxidation resistance of M05Si3 and the relative density decreasing of 0. 8% La2O3-Mo5Si3/MoSi2 composite.展开更多
文摘The oxidation behavior of 0. 8% La2O3- Mo5Si3/MoSi2 composites at 1200℃ in air was investigated. The results reveal that the oxidation resistance of the material with 0. 8% La2O3 and Mo5Si3 is impaired. The oxidation resistance is decreased with increasing Mo5Si3 content. The mass loss follows a linear law in the initial oxidation. With oxidation time prolonging, a continuous and dense oxidation scale prevents oxygen from diffusing increasing when and leads to mass change a Mo5Si3 content is less than 30%. However, the composite shows ＂PEST＂ with the addition of 40% Mo5Si3. With increasing Mo5Si3 content, the oxidation resistance of 0.8% La2O3- Mo5Si3/MoSi2 decreases. This attributes to the poor oxidation resistance of M05Si3 and the relative density decreasing of 0. 8% La2O3-Mo5Si3/MoSi2 composite.