A single crystal Ni-based superalloy AM3 was processed at withdraw rates of 3.5, 10, 50, 100, 200, and 500 μm·s-1, respectively.The as-cast microstructures and solidification segregation ratio were characterized...A single crystal Ni-based superalloy AM3 was processed at withdraw rates of 3.5, 10, 50, 100, 200, and 500 μm·s-1, respectively.The as-cast microstructures and solidification segregation ratio were characterized with various withdraw rates.The shape and size of carbide microstructures were determined.As expected, the primary and secondary dendrite arm spacings (PDAS and SDAS) decrease with the increase of withdraw rate.The highest volume fraction of eutectic γ/γ' is observed at the 100 μm·s-1 withdraw rate.The volume fraction of eutectic γ/γ' does not appear to be a strong function of the withdraw rate.With increasing withdraw rate, interface morphologies change in the sequence of planar, cellular, and dendrite.There is a general refinement of the microstructure as the withdraw rate increases.EPMA analysis showed that withdraw rate does not have obvious influence on the segregation of elements.展开更多
The microstructure of experimental nickel-base single crystal superalloys with different levels of carbon has been studied. The results indicated that with increasing carbon addition, the liquidus temperature decrease...The microstructure of experimental nickel-base single crystal superalloys with different levels of carbon has been studied. The results indicated that with increasing carbon addition, the liquidus temperature decreased obviously and the as-cast microstructures exhibited a decrease in the amount of γ/γ′ eutectic structure and an increase in the volume fraction of carbides. The carbides formed in these alloys were most script-type MC carbides which appeared continuous dendritic networks in the interdendritic region. The segregation behavior of element W was influenced by the carbon addition.展开更多
基金supported by the National Natural Science Foundation of China (Grant No.50771081,50931004)the National Basic Research Program of China (2010CB631202)
文摘A single crystal Ni-based superalloy AM3 was processed at withdraw rates of 3.5, 10, 50, 100, 200, and 500 μm·s-1, respectively.The as-cast microstructures and solidification segregation ratio were characterized with various withdraw rates.The shape and size of carbide microstructures were determined.As expected, the primary and secondary dendrite arm spacings (PDAS and SDAS) decrease with the increase of withdraw rate.The highest volume fraction of eutectic γ/γ' is observed at the 100 μm·s-1 withdraw rate.The volume fraction of eutectic γ/γ' does not appear to be a strong function of the withdraw rate.With increasing withdraw rate, interface morphologies change in the sequence of planar, cellular, and dendrite.There is a general refinement of the microstructure as the withdraw rate increases.EPMA analysis showed that withdraw rate does not have obvious influence on the segregation of elements.
基金supported financially by the National Natural Science Foundation of China (Grant No. 50771081,50931004)the National Basic Research Program of China (2010CB631202)
文摘The microstructure of experimental nickel-base single crystal superalloys with different levels of carbon has been studied. The results indicated that with increasing carbon addition, the liquidus temperature decreased obviously and the as-cast microstructures exhibited a decrease in the amount of γ/γ′ eutectic structure and an increase in the volume fraction of carbides. The carbides formed in these alloys were most script-type MC carbides which appeared continuous dendritic networks in the interdendritic region. The segregation behavior of element W was influenced by the carbon addition.